Abstract:A series of zinc (Zn) doped Fe3O4 nanoparticles with different Zn concentrations represented as ZnxFe3-xO4 (0 < x <= 1) were synthesized by the chemical coprecipitated technique mainly in the presence of sodium dodecyl benzene sulfonate (SDBS) as one of the surface modifiers. The prepared zinc-doped Fe3O4 nanoparticles were characterized by a vibrating sample magnetometer (VSM), wide-angle X-ray diffraction (WAXD), and transmission electron microscopy (TEM). The VSM measurements showed that magnetization vs applied magnetic field for zinc-doped particles showed an increasing curve with very small hysteresis and that the saturation magnetization (M-s) of ZnxFe3-xO4 reached a maximum 80.93 emu/g at x = 0.2. The experimental result exhibited that Zn0.2Fe2.8O4 nanoparticles coated with different surface modifiers give good dispersivity and outstanding stability in the organic dispersed phase compared with noncoated particles. The value of M-s decreased with further increase in x beyond 0.2. Such decreasing behavior of the magnetization was elucidated on the basis of two factors. One was the comparison between experimental and calculated curves of the average magnetic moment of paramagnetism associated with superexchange interactions among magnetic ions in tetrahedral space (A-site) and octahedral space (B-site) in a crystal unit with face-centered cubic inverse-spinel structure. The second was x-dependence on the WAXD curve profile calculated based on the modified Laue function for a diffraction peak from the (311) plane. The observed and calculated WAXD intensity curves revealed that the a-axis became longer and the corresponding crystal size became smaller with increasing x up to 0.4. In contrast, further increase beyond 0.4 provided the inverse relationships. The a-axis became shorter, and the crystal size became bigger. They were dose to those of Fe3O4 at x = 1, indicating that x = 0.4 is the zinc doping limit to form a zinc-doped Fe3O4 crystal structure.

Effects of Crystal Size and Sphere Diameter on Static Magnetic and Electromagnetic Properties of Monodisperse Fe3O4 Microspheres

Control Synthesis and Characterization of Monodispersed gamma-Fe2O3 Nanoparticles

Temperature Effects on Magnetic Properties of Fe3O4 Nanoparticles Synthesized by the Sol-Gel Explosion-Assisted Method

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Preparation and characterization of monodispersed Fe3O 4 sub-microspheres | Preparation and characterization of monodispersed Fe3O 4 sub-microspheres

A Time-Saving Method to Prepare Monodisperse Fe3O4 Microspheres with Controllable Sizes and Morphologies

Magnetic Behavior Of Zn-Doped Fe3o4 Nanoparticles Estimated In Terms Of Crystal Domain Size

Size dependent electromagnetic properties of Fe 3 O 4 nanospheres

Effects of Amount of Benzyl Ether and Reaction Time on the Shape and Magnetic Properties of Fe3o4 Nanocrystals

Hierarchically Nanostructured Fe3O4 Microspheres and Their Novel Microwave Electromagnetic Properties

Facile Synthesis of Size-Controllable Monodispersed Ferrite Nanospheres

Shape-tuned Synthesis of Dispersed Magnetite Submicro Particles with Good Magnetic Properties

Controllable Synthesis and Magnetic Properties of Monodisperse Fe3o4 Nanoparticles

Synthesis and microwave absorption properties of hollow Fe3O4 microspheres

Preparation and Characterization of Monodispersed Fe_3O_4 Sub-microspheres

Synthesis of Magnetite Submicrospheres with Tunable Size and Superparamagnetism by A Facile Polyol Process

Magnetic Properties and Exchange Bias Effect of Nano-Structure Co-X Fe-3 (-) (X) O-4 Porous Microspheres

One-Pot Hydrothermal Synthesis of Highly Monodisperse Water-Dispersible Hollow Magnetic Microspheres and Construction of Photonic Crystals

The Influence of Hollow Structure on the Magnetic Characteristics for Fe3O4 Submicron Spheres

Preparation and Characterization of Monodispersed Fe3O4 Sub-microspheres

Simultaneous acquisition of Fe<sub>3</sub>O<sub>4</sub> monocrystals: Tunable magnetic properties with various morphologies