Low Temperature Molten Salt Synthesis of YAG: Ce Spherical Powder and Its Thermally Stable Luminescent Properties after Post-Annealing Treatment

Ming Li,Ding Zhou,Cui Ping Li,Zhe Zhao

DOI: https://doi.org/10.1016/j.mssp.2015.12.028

IF: 4.1

2016-01-01

Materials Science in Semiconductor Processing

Abstract:Spherical YAG: Ce particles were successfully synthesized at 350°C by the molten-salt method. The effect of temperature and amount of salt on the crystallization and particle size of YAG: Ce were investigated thoroughly. The results demonstrated that the powders prepared at 350°C in salt to reactant ratio 2:1 were pure YAG: Ce phase with 200–300nm in particle size. The as-synthesized phosphors were later post annealed at 1200°C in O2, air and N2, respectively. The results showed that the emission intensity of YAG: Ce sensitively depended on the post-treated atmosphere and the phosphor annealed in N2 showed the highest emission intensities and a good thermal stability.