Abstract:Fatigue delamination damage is one of the most important fatigue failure modes for laminated composite structures. However, there are still many challenging problems in the development of the theoretical framework, mathematical/physical models, and numerical simulation of fatigue delamination. What is more, it is essential to establish a systematic classification of these methods and models. This article reviews the experimental phenomena of delamination onset and propagation under fatigue loading. The authors reviewed the commonly used phenomenological models for laminated composite structures. The research methods, general modeling formulas, and development prospects of phenomenological models were presented in detail. Based on the analysis of finite element models (FEMs) for laminated composite structures, several simulation methods for fatigue delamination damage models (FDDMs) were carefully classified. Then, the whole procedure, range of applications, capability assessment, and advantages and limitations of the models, which were based on four types of theoretical frameworks, were also discussed in detail. The theoretical frameworks include the strength theory model (SM), fracture mechanics model (FM), damage mechanics model (DM), and hybrid model (HM). To the best of the authors' knowledge, the FDDM based on the modified Paris law within the framework of hybrid fracture and damage mechanics is the most effective method so far. However, it is difficult for the traditional FDDM to solve the problem of the spatial delamination of complex structures. In addition, the balance between the cost of acquiring the model and the computational efficiency of the model is also critical. Therefore, several potential research directions, such as the extended finite element method (XFEM), isogeometric analysis (IGA), phase-field model (PFM), artificial intelligence algorithm, and higher-order deformation theory (HODT), have been presented in the conclusions. Through validation by investigators, these research directions have the ability to overcome the challenging technical issues in the fatigue delamination prediction of laminated composite structures.

Review of Damage Tolerant Analysis of Laminated Composites

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Review of delamination predictive methods for low speed impact of composite laminates

A Review of Delamination Damage of Composite Materials

Simulation and analysis of delamination damage propagation in CFRP structures

A novel damage characterization approach for laminated composites in the absence of material and structural information

Review On Methodologies Of Progressive Failure Analysis Of Composite Laminates

Damage Evolution of Sandwich Composite Structure Using A Progressive Failure Analysis Methodology

Finite element analysis on impact response and damage mechanism of composite laminates under single and repeated low-velocity impact

Progressive Damage Behavior of Composite L‐stiffened Structures with Initial Delamination Defects under Uniaxial Compression: Experimental and Numerical Investigations

A Micromechanics-Based Damage Model for Compressive Behavior Analysis of Impacted Composite Laminates

Review and Assessment of Fatigue Delamination Damage of Laminated Composite Structures

A Delamination Propagation Model for Fiber Reinforced Laminated Composite Materials

Predicting delamination in composite structures

Progressive damage analysis of green composite laminates subjected to in-plane crashworthiness

Finite element analysis of dynamic progressive failure of carbon fiber composite laminates under low velocity impact

Numerical Prediction of Damage Interaction during L-Shaped Laminated Composite Structures Unfolding

Analysis of the Damage Parameters Impact of Reinforced Composite Materials Initial Delamination

Application of a delamination model to laminated composite structures

Analysis of interlaminar stress concentration in laminated structure - A review

Research progress of composite laminate with delamination damage in aerospace fields