Abstract:Stress corrosion cracking (SCC) is one of the main ageing mechanism in light water reactor (LWR). 316L austenitic stainless steel was adopted in nuclear industry for its relatively high corrosion resistance. The SCC of austenitic stainless steel may occur as it is subjected to both the tensile stress and the caustic medium, with regard to maintaining the structural integrity of components in nuclear power plant, an accurate prediction and efficient assessment of the component lifetime is significant and necessary. The stress corrosion crack propagation behavior of the 316L stainless steel elbow of nuclear power plant was investigated through a numerical simulation method. Firstly a finite element (FE) model was created for the stainless steel thick-walled elbow (the outer diameter is 355.6 mm, the inner diameter is 275.6 mm), with a semi-elliptical shaped 3D defect introduced at the internal surface of the elbow as the geometry of the crack, which was consistent with a practical crack, the crack opening displacement (delta(i)) was determined by the calculations through the Dugdale model; subsequently, according to the FE calculation results, establish the fitting formula of the stress intensity factor (K) varying with the crack depth (a) and additional stress (P), and the fitting formula of the stress corrosion crack propagation rate (da/dt) for elbows under two types of cold work deformation was deduced through the combination with the experimental data, the crack propagation time was then calculated using a iterative method for cracks which evolved from different initial crack depth values to certain crack depth values. The calculation results provided effective reference criterion for the nuclear power plant safety assesment. This investigation demonstrated that, when the cold deformation extent of the elbow part is relatively small (with the hardness of 230 similar to 245 HV) and it is under the ideal condition (no initial additional stress), it takes around 57 a for the stress corrosion crack to penetrate the elbow, when the initial additional stress was elevated to 200 MPa, the elbow failure time was shrinked to 1/5 (no stress release), 2/7 (half-stress release) and 3/7 (total stress release) of the former; keep the same initial additional stress (200 MPa) and increase the cold work deformation extent (the hardness was increased from 230 similar to 245 HV to 275 similar to 300 HV), the elbow failure time was shortened to 2/5 (no stress release), 3/8 (half-stress release) and 1/3 (total stress release) for the elbow part with higher cold deformation extent compared to the part with lower cold deformation extent, thus it was observed that both the decrease of the extent of stress relaxation and the increase of the extent of cold work deformation contributed to the reduction of the residual life of the nuclear power plant 316L stainless steel elbow.

Modelling Electrical Corrosion Potential of 304 Stainless Steel under Fusion Power Plant Environment

Corrosion Fatigue Model of Austenitic Stainless Steels Used in Pressurized Water Reactor Nuclear Power Plants

A Coupled Electro-Chemo-Mechanical Model for the Stress Corrosion Cracking Prediction of Stainless Steel in High-Temperature Water

Life Prediction for Stress Corrosion Behavior of 316l Stainless Steel Elbow of Nuclear Power Plant

Electrochemical Corrosion Behaviors of 316 L Stainless Steel Used in PWR Primary Pipes

Corrosion behaviour of 316L stainless steel and anti-corrosion materials in a high acidified chloride solution

CORROSION FATIGUE OF NUCLEAR-GRADE STAIN- LESS STEEL IN HIGH TEMPERATURE WATER AND ITS ENVIRONMENTAL FATIGUE DESIGN MODEL

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

Predictions of Hydrodynamic Characteristics and Corrosion Rates Using CFD in the Piping Systems of Pressurized-Water Reactor Power Plant

Development of a finite element model for simulation and prediction of mechanoelectrochemical effect of pipeline corrosion

Microscopic Analysis of Intergranular Corrosion of 316L Stainless Steel

Study on Irradiation Assisted Stress Corrosion Cracking of Nuclear Grade 304 Stainless Steel

Erosion-Corrosion of AISI 302 Stainless Steel Sudden Expansion Pipes in High Salt Wastewater: Effect of Fluid Flow on Different Positions of a Sudden Expansion Pipe

Predicting the Wall Thinning Engendered by Erosion–corrosion Using CFD Methodology

Evaluation of Stress Corrosion Cracking Susceptibility of Forged 316 Stainless Steel in Simulated Primary Water

Electrochemical Impedance Studies for Intergranular Corrosion of Super 304H Stainless Steel

Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone

Some Fundamental Understandings of Zn-injection Water Chemistry on Material Corrosion in Pressurized Water Reactor Primary Circuit

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Assessment by finite element modelling of the mechano-electrochemical interaction at double-ellipsoidal corrosion defect with varied inclinations on pipelines

Finite element modeling of corrosion defect growth and failure pressure prediction of pipelines