Abstract:This article focuses on finding alternatives to CaF2‐containing submerged arc welding fluxes, without a compromise on the thermophysical properties. Three compositions in the CaO–MnO–SiO2–Al2O3 system with varying MnO content are identified as they seem to comply with the required melting behavior. This was estimated using the high‐temperature microscopy, DTA, simulations using FactSage (version8.3) and was found to be comparable with a commercial CaF2 containing welding flux. In addition, simulations using FactSage show the desirable dissolution of Si, Mn and weld pool O content (40–70 ppm) CaF2 has been a very common constituent in the fluxes used for welding of low‐carbon steel plates, owing to its strong ability to lower the liquidus temperature as well as viscosity of the molten flux. But the adverse impact of fluoride evaporation from molten slag on the health of operating personnel and the environment has prompted a worldwide effort to replace CaF2 with more benign constituents. Three compositions with varying MnO concentration in the CaO–MnO–SiO2–Al2O3 system, identified in the current work, have shown promise in terms of ability to control oxygen transfer and modify inclusion generation in the molten metal during the welding of low carbon low alloy steels. However, the melting behavior of a flux needs to be established before recommending its use for welding. Three compositions, with varying MnO concentration, are chosen in the current work. Aided by experimental measurements using high‐temperature microscopy, DTA and simulations using the commercially available thermodynamic package FactSage (version 8.3), this work aims to understand the melting characteristics of the developed fluxes. These characteristics seem to be comparable with a commercial CaF2‐containing welding flux, used as a reference for comparison. In addition, simulations using FactSage suggest that transfer of dissolved O, Si and Mn to the weld metal, while using these fluxes, would be benefitial to performance of the welded joint.

Unraveling Oxygen Transfer Behavior in Submerged Arc Welding Using CaF2-SiO2-CaO Fluxes

Advancing Methodologies for Elemental Transfer Quantification in The Submerged Arc Welding Process: A Case Study of CaO-SiO2-MnO Flux

Element Transfer Behavior for CaF2-Na2O-SiO2 Agglomerated Flux Subject in Submerged Arc Welding Process

Improving the Accuracy of Silicon Transfer Prediction in Submerged Arc Welding: A Multi-Reaction-Zone Analysis

Probing Element Transfer Behavior during the Submerged Arc Welding Process for CaF2-SiO2-Na2O-Cr2O3 Agglomerated Fluxes: A Thermodynamic Approach

Thermodynamic Insights into the Influence of Welding Current on Oxygen Levels in the Submerged Arc Welding Process

Thermodynamic Nature of SiO2 and FeO in Flux O Potential Control Subject to Submerged Arc Welding Process

Optimizing Elemental Transfer Predictions in Submerged Arc Welding via CALPHAD Technology under Varying Heat Inputs: A Case Study into SiO2-Bearing Flux

Elucidating the effect of Al2O3/SiO2 mass ratio upon SiO2-MnO-CaF2-Al2O3-based welding fluxes: Structural analysis and thermodynamic evaluation

Melting Behavior of a CaO–SiO2–Al2O3 Flux with Varying MnO Concentration for Use in Fusion Welding of Low‐Carbon Steel

In Situ Modification of CaF2-SiO2-Al2O3-MgO Flux Applied in the Aluminium-Assisted Transfer of Titanium in the Submerged Arc Welding of Carbon Steel: Process Mineralogy and Thermochemical Analysis

A Review on Parallel Development of Flux Design and Thermodynamics Subject to Submerged Arc Welding

A structure-oriented elucidation for viscous flow of SiO2-MnO-Al2O3 fused submerged arc welding fluxes

Modification of Flux Oxygen Behaviour via Co-Cr-Al Unconstrained Metal Powder Additions in Submerged Arc Welding: Gas Phase Thermodynamics and 3D Slag SEM Evidence

Advancing Manganese Content Prediction in Submerged Arc Welded Metal: Development of a Multi-Zone Model via the Calphad Technique

A coupled mathematical model and experimental validation of oxygen transport behavior in the electro-slag refining process

Effect of Water Flow on the Arc Stability and Metal Transfer in Underwater Flux-Cored Wet Welding

NON-EQUILIBRIUM STATIONARY STATE IN CHEMICAL REACTION OF SiO 2 /fe AT INTERFACE OF SLAG/METAL AND ITS STABILITY DURING ARC WELDING

SiO2-bearing Fluxes Induced Evolution of γ Columnar Grain Size

Understanding the Effect of Oxygen on Weld Pool and Keyhole in Laser Beam Welding

A Novel Strategy to Prevent Hydrogen Charging Via Spontaneously Molten-Slag-covering Droplet Transfer Mode in Underwater Wet FCAW