Abstract:Abstract To meet the requirements of automatic production, a new type of green BAl88Si cored solder was developed. The lap brazing experiments were carried out with copper and aluminum as brazing substrates. The microstructure, phase composition, and corrosion behavior of solder joint interface were studied by field emission scanning electron microscopy, energy dispersive spectroscopy, transmission electron microscopy, electron backscattering diffraction, tensile testing machine, and electrochemical workstation. The results show that the brazing joint of Cu/BAl88Si/Al is metallurgical bonding, and the brazing joint of Cu/BAl88Si/Al is composed of Cu 9 Al 4 , CuAl 2 , a-Al, (CuAl 2 + a-Al + Si) ternary eutectic. In addition, there is no obvious preference for each grain in the brazing joint, and there are S texture {123} , Copper texture {112} , and Brass texture {110} . The interface of Cu 9 Al 4 /CuAl 2 is a non-coherent crystal plane and does not have good lattice matching. The average particle size of CuAl 2 is 11.95 μm and that of Al is 28.3 μm. However, the kernel average misorientation (KAM) value at the brazed joint interface is obviously higher than that at the brazed joint interface copper, so the defect density at the brazed joint interface aluminum is higher than that at the brazed joint interface copper. At the same time, due to poor corrosion resistance at the interface on the aluminum side of the brazed joint, serious corrosion spots and corrosion cracks occur at the same time, which leads to the shear performance of the brazed joint decreasing by about 75% after salt spray test for 240 h.

Study on Weld Seam Surface Deposits of Cusi3 Cmt Brazing

Study on weld defects sensitivity of CMT brazing galvanized steel sheets

Microstructure and mechanical performance of depositing CuSi3 Cu alloy onto 30CrMnSi steel plate by the novel consumable and non-consumable electrodes indirect arc welding

Study on the influence of tool rotational speeds/welding traverse speeds on the quality and surface formation of 6mm copper friction stir welding

Investigating the effect of WC reinforcements in Cu Ti composite filler on the microstructural evolution and mechanical characteristics in brazing C f /SiC and GH3536

Microscopic Bonding Mechanism of Welding Interface with Molten Cu–4Zn Deposited on Solid-State Steel

Experimental Study of Cu/Fe Underwater Self-Constrained Explosive Welding Tube

Wetting Behaviors of Al-Si-Cu-Mg-Zn Brazing Materials on 5083 Aluminum Alloy

Achieving ultrafine grain strengthening C f /SiC-GH3536 joints brazed with Cu-Ti-WC composite interlayer via cold spray additive manufacturing

Effect of droplet transition on arc morphology, Mn evaporation and microstructure during the CMT welding with high nitrogen Cr-Mn steel

Microstructure, Chemical Composition and Local Corrosion Behavior of a Friction Stud Welding Joint

A Strategy to Fabricate Strength-Ductility Enhanced Braze Filler Reinforced by 3-Dimensional Graphene Sponge for Joining C/C Composites

Investigating the Effect of WC Reinforcements in Cu Ti Composite Filler on the Microstructural Evolution and Mechanical Characteristics in Brazing Cf/SiC and GH3536

Exploring avoiding brittle compounds in brazed joints of C/C composites and DD3 alloys through surface modification

Microstructure and Performance of the Cu/Al2O3 Joint Brazed with Active Composite Filler

Study on Forming Mechanism of Appearance Defects in Rotating Arc Narrow Gap Horizontal GMAW

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

Research on Cu-6.6%Al-3.2%Si Alloy by Dual Wire Arc Additive Manufacturing

Simulation Study on Weld Formation in Full Penetration Laser + MIG Hybrid Welding of Copper Alloy

Wetting mechanisms in the mass transfer process of CuSi3 droplets on the TC4 and 304SS multi-metal system controlled by the hybrid shielding gas atmosphere

Phase analysis and corrosion behavior of brazing Cu/Al dissimilar metal joint with BAl88Si filler metal