Abstract:Purpose To fabricate a selective laser melting (SLM)-processed AlSi10Mg part with almost full density and free of any apparent pores, this study aims to investigate the effect of ambient argon pressure and laser scanning speed on the particles splash during the AlSi10Mg powder bed laser melting. Design/methodology/approach Based on the discrete element method (DEM), a 3D model of random distribution of powder particles was established, and the 3D free surface of SLM forming process was dynamically tracked by the volume of fluid, where a Gaussian laser beam acts as the energy source melting the powder bed. Through the numerical simulation and process experimental research, the effect of the applied laser power and scanning speed on the operating laser melting temperature was studied. Findings The process stability has a fundamental role in the porosity formation, which is process-dependent. The effect of the processing conditions on the process stability and the resultant forming defects were clarified. Research limitations/implications The results shows that the pores were the main defects present in the SLM-processed AlSi10Mg sample, which decreases the densification level of the sample. Practical implications The optimal processing parameters (argon pressure of 1,000 Pa, laser power of 180 W, scan speed of 1,000 mm/s, powder layer thickness of 35 µm and hatch spacing of 50 µm ) applied during laser melting can improve the quality of selective laser melting of AlSi10Mg, Social implications It can provide a technological support for 3D printing. Originality/value Based on the analysis of the pore and balling formation mechanisms, the optimal processing parameters have been obtained, which were argon pressure of 1,000 Pa, laser power of 180 W, scan speed of 1,000 mm/s, powder layer thickness of 35 µm and hatch spacing of 50 µm. Then, a near-fully dense sample free of any apparent pores on the cross-sectional microstructure was produced by SLM, wherein the relative density of the as-built samples is larger than 97.5%.

Forming and Defect Analysis for Single Track Scanning in Selective Laser Melting of Ti6Al4V

Numerical Study of the Pore Defects Formation Mechanisms in Selective Laser Melting Process

X-ray CT analysis of the influence of process on defect in Ti-6Al-4V parts produced with Selective Laser Melting technology

A Thermo-Metallurgical-mechanical Model for Selective Laser Melting of Ti6Al4V

Analysis of Processing Parameters and Characteristics of Selective Laser Melted High Strength Al-Cu-Mg Alloys: from Single Tracks to Cubic Samples

Finite Element Analysis of Thermal Behavior and Experimental Investigation of Ti6Al4V in Selective Laser Melting

Experimental investigation into the single-track of selective laser melting of IN625

Multi-Physics Modeling of Single/Multiple-Track Defect Mechanisms in Electron Beam Selective Melting

Process parameter optimization for selective laser melting Ti-6Al-4V with high layer thickness

Defect Formation Mechanisms in Selective Laser Melting: A Review

A review on the simulation of selective laser melting AlSi10Mg

A Numerical Study on the Mesoscopic Characteristics of Ti-6Al-4V by Selective Laser Melting

Direct Manufacturing of Cu-based Alloy Parts by Selective Laser Melting

Effect of Processing Parameters on Forming Defects During Selective Laser Melting of AlSi10Mg Powder

Investigation on the Relationships among Process Parameters, Molten Pool Characteristics, and Fabrication Quality of Ti-10V-2Fe-3Al by Laser Direct Energy Deposition

Towards understanding metallurgical defect formation of selective laser melted wrought aluminum alloys

Coupling Analysis on Microstructure and Residual Stress in Selective Laser Melting (SLM) with Varying Key Process Parameters

Effects of Defects and Microstructures on Tensile Properties of Selective Laser Melted Ti6Al4V Alloys Fabricated in the Optimal Process Zone

Mathematical Model of Ti-6Al-4V Single Track Formed by Selective Laser Melting

Role of Scanning Strategy on Residual Stress Distribution in Ti-6Al-4V Alloy Prepared by Selective Laser Melting

Effects of the processing parameters on the forming quality of stainless steel parts by Selective Laser Melting