Study on Effects of pH Value and Oxygen Scavenger on Corrosion Rate of Carbon Steel in Softened Water Solution

chen lirong,han weihai,jiang qinghong,wang zhe

DOI: https://doi.org/10.16490/j.cnki.issn.1001-3660.2015.07.020

2015-01-01

Abstract:Objective To research the deoxidization capacity of deoxidants acetaldoxime and sodium hexametaphosphate in softened water and the effect of sodium hexametaphosphate and acetaldoxime and p H value on the corrosion inhibiting capacity of carbon steel targeting at the quality of heating softened water. Methods The deoxidizing test,the static coupon test and the rotary coupon test were used to investigate the effects on corrosion rate of sodium hexametaphosphate and acetaldoxime,adjusting p H value with sodium hydroxide and sodium carbonate and adjusting p H = 11 after deoxidization for carbon steel. Results Under the condition of doses of 160 mg / L acetaldoxime and sodium hexametaphosphate,the deoxidization rate was 45. 68% and 71. 83%,the corrosion rate was 0. 1948 mm / a and 0. 0728 mm / a. The corrosion rate was 0. 0751 mm / a and 0. 0143 mm / a with sodium hydroxide and sodium carbonate adjusting p H to 11. And under the condition of p H = 11 adjusted by doses of 120 mg / L acetaldoxime and sodium hexametaphosphate,the corrosion rate was 0. 0885 mm / a and 0. 0365 mm / a,while the corrosion rate was 0. 1531 mm / a at a dose of 140 mg / L acetaldoxime,p H = 11. Conclusion The deoxygenation rate by sodium hexametaphosphate was better than by acetaldoxime,the corrosion rate of carbon steel decreased with addition of sodium hexametaphosphate,fluctuated with addition of acetaldoxime when acetaldoxime was more than 120 mg / L,and decreased with the increasing of p H value.