Abstract:Objectives: As promising alternative to current metallic biomaterials, the porous Mg scaffold with a 3-D open-pore framework has drawn much attention in recent years due to its suitable biodegradation, biocompatibility, and mechanical properties for human bones. This experiment's aim is to study the mechanical properties, biosafety, and osteogenesis of porous Mg-Zn alloy. Methods: A porous Mg-2Zn-0.3Ca (wt%) alloy was successfully prepared by infiltration casting, and the size of NaCl particles was detected by a laser particle size analyzer. The microstructure of the Mg-2Zn-0.3Ca alloy was characterized by the stereoscopic microscope and Sirion Field emission scanning electron microscope. X-ray computerized tomography scanning (x-CT) was used to create the 3-D image. The degradation rate was measured using the mass loss method and the pH values were determined together. The engineering stress-strain curve, compressive modulus, and yield strength were tested next. The bone marrow stromal cells (BMSC) were cultured in vitro. The CCK-8 method was used to detect the proliferation of the BMSC. Alkaline phosphatase (ALP) and alizarin red staining were used to reflect the differentiation effects. After co-culturing, cell growth on the material's surface was observed by scanning electron microscope (SEM). The cell adhesion was tested by confocal microscopy. Results: The obtained results showed that by using near-spherical NaCl filling particles, the porous Mg alloy formed complete open-cell foam with a very uniform size of pores in the range of 500-600 mu m. Benefitting from the small size and uniform distribution of pores, the present porous alloy exhibited a very high porosity, up to 80%, and compressive yield strength up to 6.5 MPa. The degradation test showed that both the pH and the mass loss rate had similar change tendency, with a rapid rise in the early stage for 1-2 day's immersion and subsequently remaining smooth after 3 days. In vitro cytocompatibility trials demonstrated that in comparison with Ti, the porous alloy accelerated proliferation in 1, 3, 5, and 7 days (P < 0.001), and the osteogenic differentiation test showed that the ALP activity in the experimental group was significantly higher (P = 0.017) and has more osteogenesis nodules. Cell adhesion testing showed good osteoconductivity by more BMSC adhesion around the holes. The confocal microscopy results showed that cells in porous Mg-based alloy had better cytoskeletal morphology and were larger in number than in titanium. Conclusions: These results indicated that this porous Mg-based alloy fabricated by infiltration casting shows great mechanical properties and biocompatibilities, and it has potential as an ideal bone tissue engineering scaffold material for bone regeneration.

In Vitro Studies on the Degradability, Bioactivity, and Cell Differentiation of PRP/AZ31B Mg Alloys Composite Scaffold

Comparative Study of Different Coatings on Magnesium Alloys: The Effect on MSC Proliferation and Osteogenic Differentiation

In vitro study on the effect of platelet-rich plasma on osteogenic capability of bone marrow mesenchymal stem cells

Influence of Platelet-rich Plasma on the Proliferation and Osteogenetic Differentiation of Rat Skeletal Muscle Satellite Cells on nano-HA/PLGA Composite Scaffold

In Vitro Effects of Mg-Zn Alloy on Proliferation, Differentiation and Mineralization in MC3T3-E1 Cells

In vitro and in vivo assessment of the effect of biodegradable magnesium alloys on osteogenesis

In Vitro and Vivo Biocompatibility and Degradability of Low-Alloyed Mg-Zn-Ca-MgO Composite As Bone Repair Biomaterials

Study on the angiogenesis ability of Polymethyl methacrylate-mineralized collagen/Mg-Ca composite material in vitro and the bone formation effect in vivo

Mesenchymal stem cells in PRP and PRF containing poly(3-caprolactone)/gelatin Scaffold: a comparative in-vitro study

In vitro and in vivo evaluation of MgF2 coated AZ31 magnesium alloy porous scaffolds for bone regeneration

In-Vitro Degradation Behaviors and Biocompatibility of Sodium Alginate/Platelet-Rich Plasma-Sr 2+ Porous Microcarriers

3D Printing of a Porous Zn-1Mg-0.1Sr Alloy Scaffold: A Study on Mechanical Properties, Degradability, and Biosafety

Research on the osteogenesis and biosafety of ECM-Loaded 3D-Printed Gel/SA/58sBG scaffolds

In vitro evaluation of MgSr and MgCaSr alloys via direct culture with bone marrow derived mesenchymal stem cells

Mechanical and Biological Properties of a Biodegradable Mg-Zn-Ca Porous Alloy.

Platelet-rich plasma-derived growth factors promote osteogenic differentiation of rat muscle satellite cells: in vitro and in vivo studies.

Evaluation of Demineralized Bone Matrix Particles Delivered by Alginate Hydrogel for a Bone Graft Substitute: an Animal Experimental Study

Angiogenic and Osteogenic Potential of Platelet-Rich Plasma and Adipose-Derived Stem Cell Laden Alginate Microspheres

The in Vitro and in Vivo Biological Effects and Osteogenic Activity of Novel Biodegradable Porous Mg Alloy Scaffolds

A Preliminary Study for Novel Use of Two Mg Alloys (WE43 and Mg3Gd)

Research of osteoblast-induced rat mesenchymal stem cells cocultured with beta-TCP/PLLA composite of different ratio]