Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Tuning the K+ Concentration in the Tunnels of Α-Mno2 to Increase the Content of Oxygen Vacancy for Ozone Elimination.

Catalytic Ozonation of Multiple Vocs at Low Temperature over a Potassium-Modified Mnox-Based Catalyst

Surface Oxygen Vacancy Induced Α-Mno2 Nanofiber for Highly Efficient Ozone Elimination

Thermal Annealing Induced Surface Oxygen Vacancy Clusters in α-MnO2 Nanowires for Catalytic Ozonation of VOCs at Ambient Temperature.

Achieving toluene efficient mineralization over K/ɑ-MnO2via oxygen vacancy modulation

Oxygen vacancy-mediated Mn2O3 catalyst with high efficiency and stability for toluene oxidation

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Tuning the surface oxygen vacancies of őĪ-MnO2 to enhance the kinetics of ORR and OER

Unraveling the effects of potassium incorporation routes and positions on toluene oxidation over α-MnO2 nanorods: Based on experimental and density functional theory (DFT) studies

To Promote Ozone Catalytic Decomposition by Fabricating Manganese Vacancies in ε-MnO2 Catalyst via Selective Dissolution of Mn-Li Precursors

Engineering Defective Mnδ+-OV Active Structure in Α-Mno2 for Efficient Low-Temperature CO Oxidation

Encapsulate α-MnO2 nanofiber within graphene layer to tune surface electronic structure for efficient ozone decomposition

Highly Efficient Removal of Ozone on Amorphous Manganese Oxides Modified by Alkali Metals

Simple strategy for the construction of oxygen vacancies on α-MnO2 catalyst to improve toluene catalytic oxidation

Tuning the properties of oxygen vacancy around Cu-Mn mixed oxides on dealumination Y zeolite by P-doping to achieve ultra-efficient catalytic ozonation of toluene with low ozone consumption

Regulating oxygen vacancies and hydroxyl groups of α-MnO2 nanorods for enhancing post-plasma catalytic removal of toluene

Constructing Γ-Mno2 with Abundant Oxygen Vacancies by a Chelating Agent-Assistant Strategy to Achieve High-Efficient Conversion of NO to NO2

Insight into the effects of oxygen vacancy on the toluene oxidation over α-MnO2 catalyst

Unlocking efficient and robust ozone decomposition with CNT-confined manganese oxide via synergistic electronic modulation

Crystal facet engineering of K-OMS-2 for active site identification in catalytic ozone decomposition

Construction of oxygen vacancies in δ-MnO 2 for promoting low-temperature toluene oxidation