Abstract:As a promising technology, ozone catalytic oxidation can effectively eliminate VOCs at low temperature. However, the excessive ozone consumption brings serious economic problems for industrial applications. Herein, Cu-Mn mixed oxides were supported on the dealumination Y zeolite, and the electronic metal-support interaction between the support and metal nanoparticles was enhanced through P-doping. Satisfyingly, the optimized catalyst P2-CuMn/DY achieved over 90% conversion of toluene even at a very harsh catalytic condition (30 °C, GHSV=240,000 h −1 ). Moreover, this high toluene conversion accompanying with lower ozone consumption. Compared to CuMn/DY, the ozone/toluene consumption ratio in P2-CuMn/DY decreased from ∼ 10:1 to ∼ 8.7:1. With the help of multiple various characterizations and DFT calculations, it can be found that the existence of pyrophosphate led more charge to accumulate on the surrounding metal oxides, improving the activity of oxygen vacancies. The change in the properties of oxygen vacancies enhanced the accumulation of O* species on the catalyst, improving the utilization of ozone in the catalytic reaction. This work provides a more economical strategy and guidance to design highly effective catalysts for industrial-scale VOCs eliminations.
What problem does this paper attempt to address?
The paper primarily discusses the modulation of oxygen vacancy properties in copper-manganese mixed oxides (Cu-Mn mixed oxides) on dealuminated Y zeolite through phosphorus doping (P-doping), to achieve ultra-high catalytic performance for the catalytic ozonation of toluene, while also reducing ozone consumption. Specifically, the optimized catalyst P2-CuMn/DY mentioned in the paper achieves a toluene conversion rate of over 90% under harsh catalytic conditions (30°C, gas hourly space velocity GHSV=240,000 h^-1), even at low temperatures. Moreover, compared to the undoped CuMn/DY, the ozone/toluene consumption ratio of P2-CuMn/DY decreased from about 10:1 to approximately 8.7:1, indicating that phosphorus doping improved the catalyst's ozone utilization efficiency.
The paper points out that volatile organic compounds (VOCs) are one of the main pollutants in atmospheric environmental pollution, and catalytic combustion technology is one of the most common methods for removing VOCs in industrial applications due to its high efficiency and lack of secondary pollution. However, excessively high reaction temperatures not only require more energy consumption but also pose safety hazards. In contrast, ozone catalytic oxidation (OZCO) technology can effectively remove VOCs at lower reaction temperatures (below 100°C), which has attracted widespread attention from researchers. However, high VOCs conversion rates usually require high concentrations of ozone input, which significantly increases energy consumption and economic costs in industrial applications. Therefore, how to improve the utilization efficiency of ozone while ensuring effective degradation of VOCs has become a challenge for OZCO technology.
Research has found that ozone can only participate in the degradation process of VOCs when it is decomposed into active oxygen species (O*), and oxygen vacancies in the catalyst have been identified as effective active sites for ozone decomposition. Initially, some researchers focused on how to increase the number of oxygen vacancies in the catalyst to achieve better catalytic effects, but later it was gradually recognized that the nature of oxygen vacancies might be the key factor in converting ozone into O*. For example, Yu et al. proposed the role of asymmetric oxygen vacancies in oxidation reactions, suggesting that this type of oxygen vacancy allows oxygen species to "come and go" easily on the catalyst surface, promoting the decomposition of ozone. Recently, Zhang et al. revealed the positive role of asymmetric oxygen vacancies in Cu-Ce catalysts for the oxidation of VOCs, confirming this through static and dynamic quantitative tracking.
To improve the properties of oxygen vacancies in the catalyst, common strategies include ion doping, etching, reduction, and heat treatment. Among them, defect introduction through phosphorization is considered an effective method. The P element, with its abundant valence electrons and high electronegativity, can affect the structure of oxygen vacancies by forming defective and asymmetric electronic structures. For example, Huang et al. improved the activity of oxygen vacancies in Pt/CeO2 by introducing different phosphate structures (POx). Similarly, Ma et al. changed the stability of oxygen vacancies in Bi2SiO5 through phosphate doping, achieving this goal by altering the local electronic structure. In addition, the introduction of POx is more commonly used to enhance the electronic metal-support interaction (EMSI) between the catalyst support (such as zeolite) and metal nanoparticles, controlling the structural properties of the catalyst, and is widely applied in fields such as electrocatalysis and hydrogen evolution.
The authors of this article previously reported that copper-manganese mixed oxides supported on dealuminated Y zeolite (CuMn/DY) could achieve stable and efficient degradation of toluene at low temperatures and high gas flow rates, and that the specific micro-coordination environment of Al has an important impact on the reaction system. To further enhance the catalytic activity of CuMn/DY, the paper prepared phosphorus-doped copper-manganese catalysts with different phosphate structures. Surprisingly, the toluene conversion rate of the catalyst increased again, and a higher toluene conversion rate was accompanied by lower ozone consumption. Through various characterization techniques, it was found that the acidity properties and oxygen vacancy structure of the phosphorus-doped catalyst had changed. Therefore, the effects of orthophosphate, pyrophosphate, and polyphosphate on the catalyst structure and catalytic performance are discussed in detail. In addition, in situ DRIFTS technology was used to detect the accumulation process of O* species on different catalyst surfaces and to explain the possible reaction mechanisms. This study provides new theoretical guidance for designing more efficient catalysts to achieve economic benefits of OZCO technology in industrial applications.