Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Thermal Annealing Induced Surface Oxygen Vacancy Clusters in α-MnO2 Nanowires for Catalytic Ozonation of VOCs at Ambient Temperature.

Catalytic Ozonation of Multiple Vocs at Low Temperature over a Potassium-Modified Mnox-Based Catalyst

Regulating oxygen vacancies and hydroxyl groups of α-MnO2 nanorods for enhancing post-plasma catalytic removal of toluene

Defective Ultrafine MnOx Nanoparticles Confined within a Carbon Matrix for Low-Temperature Oxidation of Volatile Organic Compounds

Simple strategy for the construction of oxygen vacancies on α-MnO2 catalyst to improve toluene catalytic oxidation

Insight into the effects of oxygen vacancy on the toluene oxidation over α-MnO2 catalyst

Tuning the K+ Concentration in the Tunnels of Α-Mno2 to Increase the Content of Oxygen Vacancy for Ozone Elimination.

Surface Oxygen Vacancy Induced Α-Mno2 Nanofiber for Highly Efficient Ozone Elimination

Oxygen vacancy-mediated Mn2O3 catalyst with high efficiency and stability for toluene oxidation

Construction of hollow sphere MnOX with abundant oxygen vacancy for accelerating VOCs degradation: Investigation through operando spectroscopycombined with on-line mass spectrometry

Oriented generation of singlet oxygen in H<sub>2</sub>O<sub>2</sub> activation for water decontamination: regulation of oxygen vacancies over -MnO<sub>2</sub> nanocatalysts

Construction of Hollow Sphere MnOX with Abundant Oxygen Vacancy for Accelerating VOCs Degradation: Investigation Through Operando Spectroscopy Combined with On-Line Mass Spectrometry

Oxygen vacancy induced MnO 2 catalysts for efficient toluene catalytic oxidation

Enhanced Low Temperature Catalytic Activity for Toluene Oxidation over Core-Shell LaMnO3@α-MnO2 Catalyst with Oxygen Vacancies

Achieving toluene efficient mineralization over K/ɑ-MnO2via oxygen vacancy modulation

Constructing Oxygen Vacancies for 8-Mno2 Based Monolithic Catalyst by Cu Intercalation to Enhance Toluene Oxidation

Constructing Oxygen Vacancies for Δ-Mno2 Based Monolithic Catalyst by Cu Intercalation to Enhance Toluene Oxidation

Enhanced Catalytic Ozonation of Toluene Using Supported MnOx/USY Via Regulating the Distribution of Aluminum Species in USY by Dealumination

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Reheat Treatment under Vacuum Induces Pre-Calcined Α-Mno2 with Oxygen Vacancy As Efficient Catalysts for Toluene Oxidation

Catalytic Ozonation of Toluene and Dichloromethane Mixture at Low Temperatures over Modified MnOx-based Catalyst