Structural Evolution And Microwave Dielectric Properties Of Article Xzn(0.5)Ti(0.5)Nbo(4)-(1-X)Zn0.15nb0.3ti0.55o2 Ceramics

Hongyu Yang,Shuren Zhang,Hongcheng Yang,Xing Zhang,Enzhu Li

DOI: https://doi.org/10.1021/acs.inorgchem.8b00873

IF: 4.6

2018-01-01

Inorganic Chemistry

Abstract:Structure and microwave properties of xZn(0.5)Ti(0.5)NbO(4)-(1 - x)Zn0.15Nb0.3Ti0.55O2 ceramics in the range of x = 0.0-1.0 were investigated. Rietveld refinement analysis and Raman spectra show that rutile- and orthorhombic-type solid solutions formed at 0-0.2 and 0.65-1, a composite at 0.2-0.64. In the solid solution regions, chemical bonds are enlarged. In this case, the Zn/Ti/Nb-O1 bond covalency and bond susceptibility are reduced, and lattice energy and thermal expansion coefficient increase along with x increases, which is mainly responsible for the development of microwave dielectric properties. Furthermore, far-infrared spectra and a classical oscillator model were used to discuss the intrinsic dielectric properties in detail. Temperature stable ceramic was obtained for x = 0.516: epsilon(r) similar to 46.11, Q x f similar to 27 031 GHz, and tau(f) similar to -1.51 ppm/degrees C, which is promising for microwave applications.