Abstract:CsPbBr3 perovskite nanowires (NWs) with various lengths and widths have attracted much attention because of their attractive optoelectronic properties in optoelectronic devices. This study provides an effective approach to get size-controllable CsPbBr3 perovskite NWs based on the hot injection method. Oleylamine was used as the solvent to control the reaction speed, and CsPbBr3 perovskite NWs with adjustable widths and lengths were obtained by controlling the reaction time at 180 degrees C. X-ray diffraction, transmission electron microscopy (TEM), high-resolution transmission electronic microscopy, optical absorption, and photoluminescence (PL) spectra were carried out to investigate the structural evolution and growth mechanism. The results show that Cs4PbBr6 nanocrystals precipitated within 10 min and their amount reduced, and alpha-CsPbBr3 nanocrystals appeared and grew with the reaction time extending to 30 min. Cs4PbBr6 nanocrystals disappeared, and alpha-CsPbBr3 NWs with a width of similar to 20 nm and a length of similar to 1 mu m were obtained when the reaction reached 60 min. Further extending the reaction time resulted in self-assembling and growth of CsPbBr3 NWs, the width of CsPbBr3 wires reached similar to 1 mu m, and the length reached similar to 100 mu m when the reaction time was 24 h. TEM images clearly showed that CsPbBr 3 NWs become wider and longer by self-assembly of CsPbBr3 nanocubes and NWs. A statistics study revealed that there is a linear relationship between the width and the reciprocal of time. The self-assembly CsPbBr3 perovskite NWs presented a high-intensity green PL around 519 nm and high PL quantum yield, which was 71.7, 76.9, 64.9, and 39.5% for the samples reacted for 10, 30, 60, and 180 min, respectively, under 375 nm laser irradiation, and the photocarrier lifetime for the sample with 180 min can reach 25.79 ns. The obtained CsPbBr3 NWs have few defects and produce less recombination during the photoemission process, which is promising for applications in the fields of optoelectronic devices, especially photodetectors, lasers, and solar cells devices.

Ligand-Mediated Synthesis Of Compositionally Related Cesium Lead Halide Cspb2x5 Nanowires With Improved Stability

Alkyl-Thiol Ligand-Induced Shape- and Crystalline Phase-Controlled Synthesis of Stable Perovskite-Related CsPb2Br5 Nanocrystals at Room Temperature.

Ligand-assisted reprecipitation synthesis of highly luminescent and stable CsPbBr3@SiO2nanoparticles with formation kinetics analysis

A novel and facile synthesis strategy for highly stable cesium lead halide nanowires

Synthesis of Size-Controllable Self-Assembled CsPbBr3 Perovskite Nanowires: Implications for Photoemission with Less Recombination

Thioacetamide-ligand-mediated Synthesis of CsPbBr3–CsPbBr3 Homostructured Nanocrystals with Enhanced Stability

Synthesis and Improved Photoluminescent Properties and Stability of Bromine‐Rich CsPbBr3 Nanocrystals Via using CTAB as Additive

Improvement in the stability of -CsPbI<sub>3</sub> nanowires enabled by lattice immobilization through the Pb-O anchor in SBA-15

Controlled Synthesis of Composition Tunable Formamidinium Cesium Double Cation Lead Halide Perovskite Nanowires and Nanosheets with Improved Stability

Synthesis of Red Cesium Lead Bromoiodide Nanocrystals Chelating Phenylated Phosphine Ligands with Enhanced Stability

Multivariant ligands stabilize anionic solvent-oriented -CsPbX<sub>3</sub> nanocrystals at room temperature

Ligand-Mediated Synthesis of Shape-Controlled Cesium Lead Halide Perovskite Nanocrystals Via Reprecipitation Process at Room Temperature

Facile synthesis of phase-adjustable CsPbBr 3 -Cs 4 PbBr 6 Composites Nanocrystals and in-situ study of phase transformation process

Vapor-Phase Epitaxial Growth of Aligned Nanowire Networks of Cesium Lead Halide Perovskites (cspbx3, X = Cl, Br, I).

Room temperature preparation of highly stable cesium lead halide perovskite nanocrystals by ligand modification for white light-emitting diodes

Improving Stability of Cesium Lead Iodide Perovskite Nanocrystals by Solution Surface Treatments

Lithium doping induced self-crystallization of CsPbBr3 nanocrystal glass with improved quantum yield and stability

Evolution and Mechanism of Cesium Lead Bromide Nanostructures in Oleylamine‐Rich System by Hot‐Injection Method

Surface-stabilized CsPbI3 Nanocrystals with Tailored Organic Polymer Ligand Binding.

Surface ligand engineering of CsPbBr3 perovskite nanowires for high-performance photodetectors

Crystalline phase-controlled synthesis of regular and stable endotaxial cesium lead halide nanocrystals