Abstract:Numerous Rh catalysts were evaluated for N2O decomposition for automotive applications. Some Rh-containing spinel materials exhibit excellent fresh activities in the absence of H2O but become inactive after hydrothermal aging or when tested in a wet feed. Rh catalysts supported on zeolites can be very active in a dry feed even after aging but are extremely sensitive to H2O. Rh/CeO2 is an exceptional catalyst for this reaction in the presence of both H2O and O-2. Hydrothermal aging (750 degrees C/20 h) significantly increases its activity. A similar activity enhancement was found by calcining the support before Rh impregnation. XPS results show a surface enrichment of Rh species on the aged Rh/CeO2 catalyst relative to the fresh catalyst. Aberration corrected STEM images reveal that Rh is buried in the bulk on the fresh catalyst and pulled out onto the surface of the support after thermal treatments. All catalysts are inhibited by H2O with the zeolite-based Rh catalysts being the worst. The aged Rh/CeO2 catalyst is less sensitive to H 2 O relative to others. DRIFTS data show that H2O sensitivity is related to catalyst hydrophilicity; a high coverage of OH groups on a catalyst reduces its N2O decomposition activity. H2TPR results show that a Rh/CeO2 catalyst can be readily reduced at < 100 degrees C. On a reduced Rh/CeO2 catalyst, near complete N2O conversion can be obtained with a lean feed at 250 degrees C for a duration equivalent to its oxygen storage capacity. The N2O-DRIFTS experiments over a pre-reduced Rh/CeO2 catalyst show that CO + sites are quickly oxidized to Ce4+ upon contacting N2O at room temperature, resulting N-2 and adsorbed O, with the latter being an efficient oxidizer. Based on these results, a N2O decomposition mechanism is proposed for the Rh/CeO2 catalyst.

Bimetallic Rh-Fe catalysts for N 2 O decomposition: effects of surface structures on catalytic activity.

Design of Bimetallic Rh-M Catalysts for N2O Decomposition: from DFT Calculation to Experimental Study

Bimetallic Au-Pd alloy catalysts for N 2O decomposition: Effects of surface structures on catalytic activity

Catalytic Decomposition of N2o over Rhox Supported on Metal Phosphates

Rhodium Encapsulated within Silicalite‐1 Zeolite as Highly Efficient Catalyst for Nitrous Oxide Decomposition: From Single Atoms to Nanoclusters and Nanoparticles

Catalytic decomposition of N<sub>2</sub>O over Rh/Zn–Al<sub>2</sub>O<sub>3</sub> catalysts

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

Catalytic Decomposition of N2O over Fe-ZSM-11 Catalysts Prepared by Different Methods: Nature of Active Fe Species

Catalytic Decomposition of N2O over Rh/Zn–Al2O3 Catalysts

Investigation of Nitrous Oxide Decomposition over Highly Active and Stable Bimetallic CoFe-MOR Zeolite Catalyst: Effective Removal and Mechanism Study

Effect of Different Skeleton Structures on N2O Decomposition from Ammonia-Fueled Engines Using Fe-based Zeolite Catalysts

N2O decomposition by mesoporous silica supported Rh catalysts

High Catalytic Activity of Magnetic FeOx/NiOy/SBA-15: the Role of Ni in the Bimetallic Oxides at the Nanometer Level

Catalytic decomposition of N<sub>2</sub>O on supported Rh catalysts

Core-alloyed Shell Structured Fe@FeCo Di-Atomic Nanoclusters Loaded in Carbon Aerogels As Efficient Bi-Functional Catalysts Towards ORR and HER

Non-thermal Plasma Synergizes High-Alkalinity Hydroxyapatite Supported RhFe Bimetallic Catalyst for Direct Catalytic Decomposition of N2O at Low Temperature

Sba-15 Based Catalysts in Catalytic N2o Decomposition in A Model Tail-Gas from Nitric Acid Plants

Rh2O3/mesoporous MOx-Al2O3 (M = Mn, Fe, Co, Ni, Cu, Ba) catalysts: Synthesis, characterization, and catalytic applications

osition of N 2 O over Rh / Zn – Al 2 O 3 catalysts †

Nature of Active Fe Species and Reaction Mechanism over High-Efficiency Fe/CHA Catalysts in Catalytic Decomposition of N2O

Enhanced N2O Decomposition on Rh/ZrO2 Catalysts through the Promotional Effect of Palladium