Abstract:The anisotropic ductile fracture behavior of a stainless steel is investigated using a combination of experiments and analysis. The material is SS-304L, an austenitic, low-carbon stainless steel, received in the form of tubes of 2.38 mm dia. and 0.15 mm thickness. The tubes are inflated under volume control in a custom apparatus. At the same time, the axial force on the tubes is kept proportional to the pressure induced by the inflation. This leads to quasi-proportional stress paths in the meridional-hoop engineering stress space. A total of 15 discrete paths are successfully tested. Stereo-type Digital Image Correlation is used to measure the strains. In every case, the tubes develop a series of instabilities before bursting. The failure is oriented along the meridional or the hoop direction of the tube, depending on which stress is greater. A mild plastic anisotropy is detected in these experiments. Hence these results are then used for calibrating the anisotropic yield criterion Yld2004-3D. This is introduced in a finite element model of the experiments, which includes a thickness imperfection designed to capture the two failure orientations observed in the experiments. The numerical model using the Yld2004-3D criterion reproduces the experiments well, e.g., it captures the experimental stress-strain and induced strain paths better than von Mises. It is then used to probe the conditions at the onset of fracture (hybrid method). It is found that most paths lead to essentially proportional loading during deformation. A significant anisotropy in the fracture behavior is detected, with the meridional-stress-dominated paths being able to develop much higher strains than the hoop-dominated ones. These results are then captured by the DF2016 ductile fracture criterion, modified to use the anisotropic yield criterion Yld91. The proposed criterion is flexible enough to represent the fracture anisotropy very well, without being unnecessarily complex. The fracture forming limit curve (i.e., the fracture envelope in strain space) predicted by the DF2016/Yld91 model is also found to be very close to the experiments. The results and findings of this work help establish a framework to reliably design components and processes when significant fracture anisotropy is expected.

Experimental Evaluation of Microvoid Characteristics and Relationship with Stress and Strain for Ductile Fracture

In-situ Three-dimensional Investigation on Micro Ductile Fracture Mechanism of Mild Steel

Effect of stress triaxiality on micro-mechanisms of void coalesence and micro-fracture ductility of materials

A Ductile Fracture Criterion Based on Three-Dimensional Void Model

Correlation of the Maximum Shear Stress with Micro-Mechanisms of Ductile Fracture for Metals with High Strength-to-weight Ratio

A New Ductile Fracture Criterion for Various Deformation Conditions Based on Microvoid Model

On the effect of strain and triaxiality on void evolution in a heterogeneous microstructure -- A statistical and single void study of damage in DP800

A STUDY ON EXPERIMENTS AND SIMULATIONS FOR DUCTILE FRACTURE OF ISOTROPIC MATERIAL USING ROUSSELIER'S DAMAGE MODEL

Anisotropic Ductile Fracture Of A Stainless Steel Under Biaxial Loading: Experiments And Predictions

Investigation of ductile damage in dual phase steel during tensile deformation by in situ X-ray computed tomography

Ductile failure modeling

Experimental techniques for ductile damage characterisation

An uncoupled ductile fracture model considering void shape change and necking coalescence

Analysis of Metallic Ductile Fracture by extended Gurson models

Modeling of Shear Ductile Fracture Considering a Changeable Cut-off Value for Stress Triaxiality

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

A multiscale investigation into the effect of grain size on void evolution and ductile fracture: experiments and crystal plasticity modeling

Experimental and Numerical Fracture Characterization of DP1180 Steel in Combined Simple Shear and Uniaxial Tension

Analysis of Ductile Fracture by Extended Unified Strength Theory

Experimental determination of the void volume fraction for S235JR steel at failure in the range of high stress triaxialities

Coupled effect of stress state and strain rate on ductile fracture of Ti6Al4V alloy