Abstract:Highlights • The high rolling temperature would impede the DRX occurrence for these final-rolled sheets. • The reduction of the volume fraction of this β phases led to the highest peak-aging hardness in R-450 °C sheet. • The precipitate chains in R-385 °C + A sheets were beneficial for strength and elongation. • The traditional precipitation characteristic in R-450 °C + A sheet was bad for elongation but good for strength. • The peak-aging R-450 °C sheet showed the highest strength, i.e. UTS of 518±17 MPa and YS of 438±18 MPa. In this investigation, a high-strength Mg-12Gd-1.0Er-0.5Zr (wt.%) alloy sheet was produced by hot extrusion (HE) and subsequent hard-plate rolling (HPR) at different temperatures. The results indicate that the microstructures of these final-rolled sheets are inhomogeneous, mainly including coarse deformed grains and dynamic recrystallized (DRXed) grains, and the volume fraction of these coarse deformed grains increases as the rolling temperature increases. Thus, more DRXed grains can be found in R-385 °C sheet, resulting in a smaller average grain size and weaker basal texture, while the biggest grains and the highest strong basal texture are present in R-450 °C sheet. Amounts of dynamic precipitation of β phases which are mainly determined by the rolling temperature are present in these sheets, and its precipitation can consume the content of Gd solutes in the matrix. As a result, the lowest number density of β phase in R-450 °C sheet is beneficial to modify the age hardening response. Thus, the R-450 °C sheet displays the best age hardening response because of a severe traditional precipitation of β' (more) and β Η / β Μ (less) precipitates, resulting in a sharp improvement in strength, i.e. ultimate tensile strength (UTS) of ∼ 518 ± 17 MPa and yield strength (YS) of ∼ 438±18 MPa. However, the elongation (EL) of this sheet reduces greatly, and its value is ∼ 2.7 ± 0.3%. By contrasting, the EL of the peak-aging R-385 °C sheet keeps better, changing from ∼ 4.9 ± 1.2% to ∼ 4.8 ± 1.4% due to a novel dislocation-induced chain-like precipitate which is helpful to keep good balance between strength and ductility.

Effect of Cryorolling and Aging Treatment on Erichsen Formability of AA7075 Sheets at Room and Cryogenic Temperatures

Edge-crack free and high mechanical properties of AA7075 sheets by using cryorolling and subsequent aging

Effects of cryorolling, room temperature rolling and aging treatment on mechanical and corrosion properties of 7050 aluminum alloy

Effect of Cryorolling and Ageing on the Microstructure and Mechanical Properties of Al 7085 Alloy

Effect of heat treatment on the microstructure and mechanical properties of cryogenic rolling 2195 Al–Cu–Li alloy

Mechanical properties of rolled and aged AA6061 sheets at room-temperature and cryogenic environments

An investigation of cryogenic-aging process attemptted to alleviate mechanical anisotropy of 7055 thick plate

The improvement of deformability in AA7075 alloy through cryogenic treatment and its correlation with microstructural evolution and FE modelling

Microstructure evolution and mechanical properties of Al−3.6Cu−1Li alloy via cryorolling and aging

Microstructure evolution, mechanical response, and corrosion resistance for a 2195 Al-Li alloy under different rolling reductions during cryorolling

Microstructure and mechanical properties of AA1050/AA6061 multilayer composites via accumulative roll bonding and cryorolling and subsequent aging

Effect of Deep Cryogenic Treatment on the Artificial Aging Behavior of 6082 Aluminum Alloy

Effects of cryogenic treatment on microstructure and mechanical properties of AZ31 magnesium alloy rolled at different paths

Improving Precipitation in Cryogenic Rolling 6016 Aluminum Alloys during Aging Treatment

Effect of thermomechanical processing on mechanical properties and microstructural evolution of Al-Mg-Zn alloy

Effects of deformation temperatures on microstructures, aging behaviors and mechanical properties of Mg-Gd-Er-Zr alloys fabricated by hard-plate rolling

Effect of Different Cryogenic Rolling Strains on the Impact Properties of 6082 Aluminum Alloy

Effect of Cryogenic Time on Microstructure and Properties of TRCed AZ31 Magnesium Alloy Sheets Rolled during Cryogenic Rolling

Tensile properties and a modified s-Johnson-Cook model for constitutive relationship of AA7075 sheets at cryogenic temperatures

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures

A comparative study on cryogenic formability and paint baking property of AA7075 alloy sheets tempered at fast retrogressed and pre-aged conditions