Shear-induced change of phase morphology and tensile property in injection-molded bars of high-density polyethylene/polyoxymethylene blends
Run Su,Juanxia Su,Ke Wang,Changyue Yang,Qin Zhang,Qiang Fu
DOI: https://doi.org/10.1016/j.eurpolymj.2008.12.009
IF: 6
2009-01-01
European Polymer Journal
Abstract:It is feasible to control the phase morphology and phase inversion for immiscible polymer blends to manipulate their properties. In this work, the blend of high-density polyethylene (HDPE)/polyoxymethylene (POM) was used as an example, to demonstrate the effect of shear on the phase morphology and resultant mechanical properties in immiscible polymer blends. To do so, a well defined “in-process morphology control” process during injection molding was conducted. That was: after making the blends via melt mixing, the injection-molded bars were prepared via a so-called dynamic packing injection molding equipment to impose a prolonged shearing on the melts during the solidification stage. Phase morphologies and crystal structures of the blends were estimated mainly through scanning electron microscopy, differential scanning calorimetry and 2D wide-angle X-ray scattering, respectively. For in-process morphology controlled samples, co-continuous structures, especially subinclusions inside another continuous phase induced by shear, were observed when the HDPE content was between 30wt% and 50wt%, leading to much early occurrence of phase inversion and also the lowest degree of orientation for both HDPE and POM. However, for samples obtained via conventional injection molding, a droplet morphology was always observed with HDPE dispersed in POM as the content of HDPE was up to 30wt%, but with POM dispersed in HDPE as the content of HDPE was 50wt%. The performances of injection-molded bars were mainly respect to the phase morphologies for samples obtained via conventional injection molding in which tensile properties continuously decreased with increasing of HDPE content up to 30wt% and then increased with further increasing of HDPE content. For the in-process morphology controlled samples, the tensile properties depended not only on the phase morphology, but more importantly on the degree of orientation. One observed only a slight decrease of tensile property as the content of HDPE was less than 15wt%, while an abrupt decrease when the content of HDPE was between 30wt% and 50wt%, probably due to the lowest degree of orientation in this composition range.