Measuring failure pressure of porous superhydrophobic coatings via microfluidic method

Min Zhang,Yuxiang Xiao,Xiangwei Lian,Ying Dong

DOI: https://doi.org/10.1007/s00339-018-1917-6

2018-01-01

Applied Physics A

Abstract:The transition of critical wetting conditions on superhydrophobic surfaces, that is, from Cassie state to Wenzel state, often indicates the failure of super-hydrophobicity on the surface. Recognizing the critical hydrostatic pressure at which a superhydrophobic surface starts departing from the Cassie state is important in the application of surfaces used under water. However, the measurement of the critical pressure for a superhydrophobic surface often involves complicated methods and systems such as optical spectroscopy and pressure vessels. This paper reports a microfluidic method for the measurement of critical failure pressure of superhydrophobic porous coatings by allowing water to penetrate the coatings from cross-sectional direction in microchannels. Two types of superhydrophobic porous coatings with different hydrophobicities, namely, titanium oxide (TiO 2 ) coatings and TiO 2 /single-walled carbon nanotube (SWNT) coatings, were fabricated inside microchannels by liquid-phase deposition and lift-off process. Experimental results show that the critical failure pressures of TiO 2 coatings decrease from 36.6 to 28.0 mBar as the porosity increases. TiO 2 /SWNT coatings with porosity of 19% show a higher failure pressure of 46.1 mBar due to its higher contact angle and lower hysteresis in comparison with TiO 2 coatings. The method presented here provides a simple way to measure the critical failure pressure of superhydrophobic coatings. Although only TiO 2 and TiO 2 /SWNT coatings were tested, any porous coating material which is compatible with lift-off process can be measured by this microfluidic method.