Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Corrosion Behavior of Low-Alloy Pipeline Steel Exposed to H2S/CO2-Saturated Saline Solution

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Effect of Temperature and H<sub>2</sub>S Concentration on Corrosion of X52 Pipeline Steel in Acidic Solutions

Corrosion Mechanism of Oil Field Gathering Pipeline Containing Small H2S Impurity

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Corrosion Investigation of Commercially Available Linepipe Steel in CO2 Environment

Influence of H2S on the general corrosion and sulfide stress cracking of pipelines steels for supercritical CO2 transportation

Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2

Research on the Corrosion Behavior of Q235 Pipeline Steel in an Atmospheric Environment through Experiment

Corrosion behaviour of X80 pipeline steel welded joint in H2O- saturated supercritical-CO2 environment

Corrosion-Mechanical Properties and Susceptibility to Hydrogenetaion of Pipe Steel in the Presence of Carbon Dioxide Gas and Hydrogen Sulphide in Environment

Main control factors and prediction model of flow-accelerated CO2/H2S synergistic corrosion for X65 steel

Unraveling the effect of H2S on the corrosion behavior of high strength sulfur-resistant steel in CO2/H2S/Cl− environments at ultra high temperature and high pressure

Effect of Ti Microalloying on the Corrosion Behavior of Low-Carbon Steel in H2S/CO2 Environment

Corrosion Behavior of Tubing in High-Salinity Formation Water Environment Containing H2S/CO2 in Yingzhong Block

Corrosion behavior study on heat treated API X70 pipeline steel exposed in different aggressive environments

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

Corrosion performance of super duplex stainless steel and pipeline steel dissimilar welded joints: a comprehensive investigation for marine structures

Electrochemical Investigation of the Corrosion Behavior of API 5L-X65 Carbon Steel in Carbon Dioxide Medium

A Mechanistic Model for Pipeline Steel Corrosion in Supercritical CO2–SO2–O2–H2O Environments