Phase structure and microwave dielectric properties of Zr(ZnNb)TiO (0.2 ≤ x ≤ 0.8) ceramics

Bin Tang,Shengquan Yu,Hetuo Chen,Shuren Zhang,Xiaohua Zhou

DOI: https://doi.org/10.1007/s10854-012-0955-7

2013-01-01

Abstract:The phase structure, morphology and microwave dielectric properties of Zr(ZnNb)TiO (0.2 ≤ x ≤ 0.8) ceramics were investigated as a function of the amount of (ZnNb) substitution by the solid-state reaction technique. X-ray diffraction analysis showed the co-existence of the solid solution ZrTiO (x = 0.2) or ZrTiO(x = 0.4–0.5) as the main phase and TiO as the second phase, and the single-phase region for substituted ZrTiO was obtained with x ≥ 0.5. As increasing x from 0.2 to 0.8, the grain growth was promoted, moreover the dielectric constant ε and the temperature coefficient of resonant frequency τ dropped from 53.8 to 39.2 and from +106.2 to −25.5 ppm/°C respectively, and the Q × f values increased from 33,200 to 43,200 GHz. Ceramics with good microwave dielectric properties: ε = 41.7, Q × f = 42,100 GHz and τ = −15.5 ppm/°C was obtained at x = 0.6.