Abstract:The high-entropy alloy coatings of FeCoCrNiCuB x (x = 0, 0.1, 0.3, 0.5, x values are molar ratios) were prepared on the surface of Q235 steel by laser cladding. The microstructure, microhardness, and surface energy of the FeCoCrNiCuB x coatings were investigated, and the tribological property and wear mechanism of the composite coatings at room temperature (RT) and 600 °C(HT) were analyzed. The FeCoCrNiCu coating consists of a single FCC-type solid solution. When x = 0.3, 0.5, the composite coatings appear the Cr 2 B phase. The x = 0.5 (B5) coating has the lowest surface energy (27.45mN/m), which is one of the reasons it has excellent tribological properties. The tribological properties of FeCoCrNiCuB x composite coatings were improved at both RT and HT. The B5 coating has excellent tribology at both RT and HT. At RT, the wear resistance of the B5 coating (wear rate is 8.54 ×10 −5 mm 3 /N∙m, coefficient of friction (COF) is 0.51) was improved by 54.79%, 50.89%, and 12.86% compared with x = 0(HEA), x = 0.1(B1), and x = 0.3(B3), respectively, the COF reduced by 42.69%, 41.39%, 22.73%. At HT the wear resistance of the B5 coating (wear rate is 6.69 ×10 −5 mm 3 /N∙m, COF is 0.24) was increased by 71.53%, 52.91%, and 49.42% compared to HEA, B1, and B3, respectively, the COF reduced by 29.41%, 25.00%, 17.24%. The wear mechanisms of coatings that add B element at RT are abrasive wear and fatigue wear, and at HT are mainly oxidative wear, moderate abrasive wear and fatigue wear.B 2 O 3 melts at HT to form a low-viscosity liquid that forms a lubricating film that isolates the contact surfaces and reduces direct contact and adhesion. This is the main reason for the excellent friction properties of B5 coating at HT.

Reduced crater wear and improved high-speed dry cutting performance of B-containing AlTiBN coatings against Ti-6Al-4 V alloy

Design and application of B-containing hard coatings for high-speed dry cutting against Ti-alloys- A review

Effects of multilayer structure on impacting fatigue resistance and high-speed dry cutting performance against Ti-6Al-4 V of AlTiN/AlTiBN multilayer coatings

Effect of Trace Boron Addition on the Microstructural Evolution and Mechanical Properties in Ti45al8nb2cr-B Alloys

Investigation of the Wear Performance of TiB2 Coated Cutting Tools during the Machining of Ti6Al4V Alloy

Effect of Al Content on the Wear Evolution of Ti1-xAlxN-Coated Tools Milling Ti-6Al-4V Alloy

Mechanics and Cutting Performance of Multilayer Nanostructured TiAlN/TiSiN/ZrN Coatings

Preparation and toughness optimization of (AlCrSiN/TiN) 20 /Ti multilayer multiscale bionic tool coatings

Properties and Performance of TiAlSiN and AlCrN Monolayer and Multilayer Coatings for Turning Ti-6Al-4V

Influence of Cutting Conditions on the Wear Resistance of Tools with a TiB2 Coating during Titanium Alloy Machining

Microstructure, mechanical properties and cutting performance of super-hard Ti(B,C,N) coatings prepared by chemical vapor deposition method

Effect of TiB2 addition on microstructure and fluidity of cast TiAl alloy

Effects of Boron Content on Microstructure and Mechanical Properties of TiAlSiBxN Nanocomposite Films

Effects of B Content on Wear and Corrosion Resistance of Laser-Cladded Co-based Alloy Coatings

Enhancing Tool Performance in High-Speed End Milling of Ti-6Al-4V Alloy: The Role of AlCrN PVD Coatings and Resistance to Chipping Wear

Improvement of Tribological Performance of TiAlNbN Hard Coatings by Adding AlCrN

Finite element analysis of Ti 1-x Al x N coated tools cutting performance and tool wear during Ti-6Al-4V milling

Controllable high adhesion and low friction coefficient in TiAlCN coatings by tuning the C/N ratio

Tribological Properties and Preparation of (Ti,Al)N Coatings on High Speed Steel Substrate

In-situ TiB2-TiC reinforced Fe-Al composite coating on 6061 aluminum alloy by laser surface modification

Effect of B addition on the microstructure and tribological properties of laser cladding FeCoCrNiCu composite coatings