Study on the High Temperature Heat Treatment Process Optimization of Different Sizes High Jc Nb 3 Sn Wire Produced by WST
Guo Qiang,Chen Jianya,Wu Bo,Shi Yigong,Li Zheng,Liu Xianghong,Feng Yong,Li Jianfeng,Zhang Pingxiang
DOI: https://doi.org/10.1109/tasc.2024.3363684
IF: 1.9489
2024-01-01
IEEE Transactions on Applied Superconductivity
Abstract:The heat treatment process plays a central role in optimizing the critical current density of Nb3Sn wire. Increasing the critical current density of Nb3Sn wire, reducing the use amount of wire in magnets and reducing the price are important ways to promote the industrialization and mass application of Nb3Sn wire. The Nb3Sn microstructure state in the wire and an even distribution of Ti are critical factors for enhancing the current density of the wire. The grain size of the Nb3Sn wire increases with the rise in heat treatment temperature. Therefore, the optimum temperature should be the lowest that ensures the full reaction/diffusion of each element.So the optimum third plateau heat treatment process of different size high Jc Nb3Sn wire is: (1) the third plateau of outer diameter 0.82 mm wire is 640 °C, and the holding time is 50 h; (2) the third plateau of outer diameter 0.99 mm wire is 665 °C, and the holding time is 50 h; (3) the third plateau of outer diameter 1.30 mm wire is 665 °C, and the holding time is 80 h. The average critical current density of the wire, measured at 12 T and 4.22 K, has been increased from 2500 A/mm2 to 2600 A/mm2.
physics, applied,engineering, electrical & electronic