Turning Waste Concrete Powder into High Calcium Alkali-Activated Cementitious Materials and Artificial Aggregates
Zhengyan Shen,Hongguang Zhu,Xiangchuan Meng,Zhijian Zhao,Qiuxiang Chang,Jiajing Wu,Zilu Lin,Qihang Chen
DOI: https://doi.org/10.1016/j.mtcomm.2024.110582
IF: 3.8
2024-01-01
Materials Today Communications
Abstract:In order to handle the environmental pollution caused by waste concrete powder, recycled concrete powder (RCP) is utilized to prepare high calcium alkali-activated cementitious materials and artificial aggregates. This study first investigates the high calcium alkali-activated cementitious materials, exploring the effects of different mineral admixtures, liquid-to-solid ratios (L/S), RCP/slag, Na2SiO3 modulus, and Na2O content. The results illustrate that slag powder is the best mineral admixture and the most critical factor affecting cementitious materials. Increasing the slag dosage enhances the generation of C-(A)-S-H, improves the microstructure, and increases compressive strength, with a maximum compressive strength reaching 68.42 MPa. According to these test results, the impact of various factors on RCP aggregates is further explored. The results illustrate that the L/S and slag content are primary factors influencing particle size distribution and strength. Increasing these factors leads to larger aggregate particle sizes and higher strength. The compressive strength of the aggregates at 7d reaches 93.24--99.5 % of that at 28d, with a maximum strength of 8.2 MPa. Additionally, slag content (10-30 %) and Na2O content significantly impact the physical properties of aggregates, improving apparent density and bulk density while reducing water absorption. To verify the applicability of RCP aggregates, they were used in concrete, and the effects of aggregate strength and replacement rate on concrete performance were explored. The results display that as aggregate strength rises, the mechanical properties of the concrete improve. When RCP aggregates are incorporated, the mechanical properties of the natural concrete decline only slightly (<16.70 %). The probability of aggregate damage increases with decreased RCP aggregate strength or increased RCP aggregate content under pressure. RCP aggregate concrete exhibits better shrinkage resistance compared to natural concrete. The process of utilizing RCP is low-energy, non-polluting, and results in high-performance products, making the large-scale effective utilization of RCP feasible.