Surface Modification of PEDOT:PSS for Enhanced Performance of Inverted Perovskite Solar Cells
Puan Lin,Wenfeng Zhang,Liuwen Tian,Lingbo Jia,Fang Wen,Gongtao Duan,Xiangqing Zhou,Shenghou Zhou,Fu Zhang,Yutong Jiang,Tao Chen,Fengguang Liu,Shangfeng Yang,Yuelong Huang
DOI: https://doi.org/10.1021/acsaem.0c03249
IF: 6.4
2021-04-28
ACS Applied Energy Materials
Abstract:Inverted perovskite solar cells (PSCs) with PEDOT:PSS as hole transporting layers exhibit tremendous prospects for flexible photovoltaic applications owing to their characteristics of low-temperature solution processability and favorable flexibility. Nevertheless, the energy level mismatch of PEDOT:PSS and perovskite layer results in a severe energy deficit. In addition, the acidity of PEDOT:PSS is detrimental to the stability of devices. To address these issues, we employ a glyceryl monostearate (GMS) interlayer to improve the work function and conductivity of PEDOT:PSS. Meanwhile, it can passivate the traps at the interface of PEDOT:PSS/perovskite. As a consequence, the champion power conversion efficiencies of photovoltaic devices based on MAPbI<sub>3</sub> films increase from 14.82% to 17.29% due to the surface modification of PEDOT:PSS with GMS, which is mainly ascribed to the enhanced open-circuit voltage and short-circuit current density. Furthermore, the nonencapsulated MAPbI<sub>3</sub> perovskite films and devices based on GMS-modified PEDOT:PSS show much better moisture stability and thermal stability than the counterparts without GMS modification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c03249?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c03249</a>.<i>W</i><sub>F</sub> of the PEDOT:PSS film via KPFM and UPS measurements; transmission spectra of the PEDOT:PSS film; AFM images of the PEDOT:PSS film without and with GMS treatment; SEM images of the MAPbI<sub>3</sub> films; contact angles; fwhm of the XRD diffraction peaks; UV–vis spectra and PL spectra of MAPbI<sub>3</sub> films deposited on different substrates; <i>J–V</i> curves of the electron-only and hole-only devices under the dark condition; electron and hole mobility of the perovskite films; photovoltaic parameters; schematic of energy level alignment; integrated <i>J</i><sub>SC</sub> obtained from the EQE; stability characterization (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c03249/suppl_file/ae0c03249_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels