A One-Step Hard-Templating Method for the Preparation of a Hierarchical Microporous-Mesoporous Carbon for Lithium-Sulfur Batteries

Niu Shu-zhang,Wu Si-da,Lu Wei,Yang Quan-hong,Kang Fei-yu

DOI: https://doi.org/10.1016/s1872-5805(17)60123-9

IF: 10.9

2017-01-01

Carbon

Abstract:Porous carbon materials can increase the conductivity of sulfur and restrain the shuttling of polysulfides in the electrolyte. A hierarchical microporous-mesoporous carbon (HMMC) with a large surface area and pore volume was prepared by the simple one-step carbonization of a mixture of magnesium gluconate (MG) and phenolic resin. The MG was transformed into nanosize magnesium oxide that acted as a hard template during carbonization to create mesopores. The HMMC has a high surface area (∼1 560 m2 g−1) and large pore volume (∼2.6 cm3 g−1), which provides abundant space for sulfur loading and accommodates volume changes during charge/discharge. The interconnected pore structure and carbon framework ensure fast electron and Li ion transfer. As the cathode of a Li-S battery the sulfur-loaded HMMC has a high discharge capacity of 939 mAh g−1 at 0.3 C and a reversible capacity of 731 mAh g−1 after 150 cycles with only a 0.15% capacity fade per cycle. Even at a high rate of 2 C, it still delivers a high discharge capacity of 626 mAh g−1, showing an excellent rate performance.