Abstract:Generally, superhydrophilic self-cleaning coatings are prepared from semiconductors with photocatalytic properties. Organic pollutants attached to the coating surface can be degraded by its photocatalytic performance realizing a self-cleaning goal. Herein, SiO2–TiO2 composite particles were fabricated by the hydrolysis and precipitation of TiOSO4, and SiO2 microspheres were chosen as carriers, which are inexpensive and environmentally friendly. Then, superhydrophilic self-cleaning SiO2–TiO2 coatings were fabricated by spraying the composites on the surfaces of substrates. The morphology, structure and self-cleaning performance of the SiO2–TiO2 coating were characterized and tested. The results revealed that nano-TiO2 was loaded on the surfaces of SiO2 microspheres uniformly forming a hierarchical micro/nanostructure. The SiO2–TiO2 composite particles exhibited excellent photocatalytic degradation performance, and the degradation rate of methyl orange (10 ppm) was more than 98% under UV irradiation for 40 min. Furthermore, the coating prepared with the SiO2–TiO2 composite particles exhibited superhydrophilicity. A water droplet spreads completely on the coating surface in 0.35 s, and the contact angle reaches 0°. In addition, rhodamine B (RhB) and methylene blue (MB) on the coating surface can be degraded efficiently under sunlight irradiation. The SiO2–TiO2 composite particles can be sprayed directly on the surfaces of concrete, brick, wood, and glass slides. Therefore, the particles showed good adaptability to different substrates. The superhydrophilic property was due to the hydrophilicity of SiO2 and TiO2, the hierarchical micro/nanostructure of the SiO2–TiO2 composites, and the photoinduced superhydrophilicity of TiO2. The above experimental results show that the as-prepared superhydrophilic self-cleaning SiO2–TiO2 coating has a large application potential.

Preparation of Nano-TiO2-Coated SiO2 Microsphere Composite Material and Evaluation of Its Self-Cleaning Property

Study on Nano- Titanium Dioxide Thin Film Coated on Self-cleaning Glass Surface

Synthesis of TiO2 Based Superhydrophobic Coatings for Efficient Anti-Corrosion and Self-Cleaning on Stone Building Surface

Fabrication of superhydrophilic self-cleaning SiO2–TiO2 coating and its photocatalytic performance

Hydrolytic Modification of SiO2 Microspheres with Na2SiO3 and the Performance of Supported Nano-TiO2 Composite Photocatalyst

Effect of calcination temperature on the structure and properties of SiO2 microspheres/nano-TiO2 composites

The Preparation of TiO2 Film by the Sol-Gel Method and Evaluation of Its Self-Cleaning Property

Study of Self-Cleaning and Low-Emission Properties of FTO/TiO2 Composite films

Preparation of TiO2/SiO2 Composite by Chemical Coating Method

Robust SiO2@TiO2 nanocoatings with antireflection and photocatalytic self-cleaning properties by introducing commercial P25 TiO2

Preparation of a temperature-sensitive superhydrophobic self-cleaning SiO2-TiO2@PDMS coating with photocatalytic activity

Preparation of a Self-Cleaning TiO2-SiO2/PFDTS Coating with Superamphiphobicity and Photocatalytic Performance

Preparation of TiO2/SiO2 Composite Nano-particles for Environmental Function Coatings

Preparation of TiO2 Composite Photocatalyst Using Amorphous SiO2 Microspheres Loaded with Spent SCR Catalysts

Formation of supra-amphiphilic self-cleaning surface through sun-illumination of titania-based nanocomposite coatings

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Preparation of Titanium Dioxide Nano Particle Modified Photocatalytic Self-Cleaning Concrete

Fabrication of hydroxyl group modified monodispersed hybrid silica particles and the h-SiO2/TiO2 core/shell microspheres as high performance photocatalyst for dye degradation

PREPARATION AND PROPERTIES OF A NANO-TiO2 COMPOSITE PHOTOCATALYST SUPPORTED BY NATURAL QUARTZ

Nano-TiO2 Decorated Radial-Like Mesoporous Silica: Preparation, Characterization, and Adsorption-Photodegradation Behavior

Preparation of a microsphere SiO2/TiO2 composite pigment: The mechanism of improving pigment properties by SiO2