Fabrication of hydroxyl group modified monodispersed hybrid silica particles and the h-SiO2/TiO2 core/shell microspheres as high performance photocatalyst for dye degradation

Zhe-Ying Shen,Long-Yu Li,Yat Li,Chang-Chun Wang

DOI: https://doi.org/10.1016/j.jcis.2010.10.023

IF: 9.9

2011-01-01

Journal of Colloid and Interface Science

Abstract:The monodisperse hybrid silica particles (h-SiO2) were firstly prepared by a modified sol–gel process and the surface was modified in situ with double bonds, then abundant carboxyl moieties were introduced onto the surface of the silica core via thiol–ene click reaction. Afterward, the h-SiO2/TiO2 core/shell microspheres were prepared by hydrolysis of titanium tetrabutoxide (TBOT) via sol–gel process in mixed ethanol/acetonitrile solvent, in which the activity of TBOT could be easily controlled. The carboxyl groups on the surface of silica particles promote the formation of a dense and smooth titania layer under well control, and the layer thickness of titania could be tuned from 12 to 100nm. The well-defined h-SiO2/TiO2 core/shell structures have been confirmed by electron microscopy and X-ray photoelectron spectroscopy studies. After calcination at 500°C for 2h, the amorphous TiO2 layer turned into anatase titania. These anatase titania-coated silica particles showed good photocatalytic performance in degradation of methyl orange aqueous solution under UV light.