Piezoelectric ceramics with high piezoelectricity and broad temperature usage range
Qinghu Guo,Fei Li,Fangquan Xia,Pengbin Wang,Xiaoyi Gao,Hua Hao,Hanxing Liu,Huajun Sun,Shujun Zhang
DOI: https://doi.org/10.1016/j.jmat.2020.11.012
IF: 8.589
2021-07-01
Journal of Materiomics
Abstract:The optimized properties <em>d</em><sub>33</sub>=720 pC/N, <em>d</em><sub>33</sub>*= 950 pm/V, <em>k</em><sub>33</sub>=0.80 and <em>T</em><sub>C</sub>=293 ºC were achieved in the studied material.High thermal stability was observed with piezoelectric variation below 20% with temperature up to 280 °C.High piezoelectric properties can be explained by the synergistic contributions of MPB and local structure heterogeneity.There is a general observation that the Curie temperature and piezoelectric property of the ferroelectric ceramics can be enhanced only at the expense of each other, i.e., higher piezoelectricity, lower Curie temperature, thus, limits their applications over broad temperature range. In this research, Sm-modified 0.15Pb(Mg<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub>-(0.85-<em>x</em>)PbZrO<sub>3</sub>-<em>x</em>PbTiO<sub>3</sub> ceramics have been studied, where excellent piezoelectric coefficients <em>d</em><sub>33</sub> = 720 pC/N, <em>d</em><sub>33</sub>*= 950 pm/V and high Curie temperature <em>T</em><sub>C</sub> = 293 °C were simultaneously achieved for <em>x</em> = 0.42 composition by designing the morphotropic phase boundary (MPB) with local structural heterogeneity. Of particular significance is that a high thermal stability was observed with piezoelectric variation below 20% with temperature up to 280 °C, demonstrating that the <em>x</em> = 0.42 composition is a good candidate for piezoelectric application over broad temperature range where high temperature stability is required. This work provides a good paradigm for designing high-performance piezoelectric ceramics with high thermal stability via a combination of MPB and local structural heterogeneity.<span class="display"><span><ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305207-fx1_lrg.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download high-res image (296KB)</span></span></a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305207-fx1.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download full-size image</span></span></a></li></ol></span></span>
materials science, multidisciplinary,chemistry, physical,physics, applied