Temperature-dependent electrical properties of 0.5Pb(NiNb)O–(0.5 − )PbTiO–PbZrO piezoceramics near the morphotropic phase boundary

Jia-Jun Zhou,Ke Wang,Jing-Feng Li,Xiao-Wen Zhang,Hong Liu,Jing-Zhong Fang

DOI: https://doi.org/10.1007/s10854-014-1907-1

2014-01-01

Abstract:0.5Pb(NiNb)O–(0.5 − )PbTiO–PbZrO ( = 0.10–0.20) polycrystalline ceramics were fabricated by solid-state reaction method. The phase structures, microstructure and temperature dependence of the electrical properties were investigated in detail. Both X-ray diffraction and Raman spectroscopy results indicated that the morphotropic phase boundary (MPB) separating tetragonal from rhombohedral phases located around the region with  = 0.14–0.16. Well-saturated ferroelectric – loops were obtained for all compositions and the compositions near MPB possessed the relative large remnant polarization  ~ 24 μC/cm and low coercive field  ~ 5 kV/cm. High performance of electric-induced-strain property with ( ) up to 1,140 pm/V could be achieved in the composition with  = 0.15. When the content of PbZrO was 14 mol%, the ceramics showed slightly lowered piezoelectric coefficient of 898 pm/V. But excellent temperature stability of piezoelectric property was exhibited that the changed <10 % when the temperature increased from room temperature to 120 °C. The piezoelectric property of this solid solution makes it promising for application in multilayer piezoactuators.