Temperature-dependent electrical properties of 0.5Pb(Ni 1/3 Nb 2/3 )O 3 –(0.5 − x )PbTiO 3 – x PbZrO 3 piezoceramics near the morphotropic phase boundary

Jia-Jun Zhou,Ke Wang,Jing-Feng Li,Xiao-Wen Zhang,Hong Liu,Jing-Zhong Fang

DOI: https://doi.org/10.1007/s10854-014-1907-1

2014-01-01

Abstract:0.5Pb(Ni 1/3 Nb 2/3 )O 3 –(0.5 − x )PbTiO 3 – x PbZrO 3 ( x = 0.10–0.20) polycrystalline ceramics were fabricated by solid-state reaction method. The phase structures, microstructure and temperature dependence of the electrical properties were investigated in detail. Both X-ray diffraction and Raman spectroscopy results indicated that the morphotropic phase boundary (MPB) separating tetragonal from rhombohedral phases located around the region with x = 0.14–0.16. Well-saturated ferroelectric P – E loops were obtained for all compositions and the compositions near MPB possessed the relative large remnant polarization P r 24 μC/cm 2 and low coercive field E c 5 kV/cm. High performance of electric-induced-strain property with d_33^* ( S max /E max ) up to 1,140 pm/V could be achieved in the composition with x = 0.15. When the content of PbZrO 3 was 14 mol