Abstract:Initial damage to a stud due to corrosion, fatigue, unexpected overloading, a weld defect or other factors could degrade the shear capacity of the stud. Based on typical push-out tests, a FEM model and theoretical formulations were proposed in this study. Six specimens with the same geometric dimensions were tested to investigate the effect of the damage degree and location on the static behavior and shear capacity of stud shear connectors. The test results indicated that a reduction of up to 36.6% and 62.9% of the section area of the shank could result in a dropping rate of 7.9% and 57.2%, respectively, compared to the standard specimen shear capacity. Numerical analysis was performed to simulate the push-out test and validated against test results. A parametrical study was performed to further investigate the damage degree and location on the shear capacity of studs based on the proposed numerical model. It was demonstrated that the shear capacity was not sensitive to the damage degree when the damage section was located at 0.5d, where d is the shank diameter, from the stud root, even if the stud had a significant reduction in area. Finally, a theoretical formula with a reduction factor K was proposed to consider the reduction of the shear capacity due to the presence of initial damage. Calculating K was accomplished in two ways: a linear relationship and a square relationship with the damage degree corresponding to the shear capacity dominated by the section area and the nominal diameter of the damaged stud. This coefficient was applied using Eurocode 4, AASHTO LRFD (2014) and GB50017-2003 ( 2003) and compared with the test results found in the literature. It was found that the proposed method produced good predictions of the shear capacity of stud shear connectors with initial damage.

Behaviour Of Corroded Single Stud Shear Connectors

Experimental Investigation and Design of Corroded Stud Shear Connectors

Behaviour of Corroded Stud Shear Connectors under Fatigue Loading

Experimental Investigation of Corroded Stud Shear Connectors Subjected to Fatigue Loading

Research on Static Behavior of Stud Shear Connectors after Strong-corrosion Based on Push-out Test

Experimental and Theoretical Investigation on the Mechanical Properties of Corroded Stud Shear Connectors

Static and Fatigue Behavior of Steel-Concrete Composite Beams with Corroded Studs

Static and Fatigue Behaviors of Corroded Stud Connectors in Weathering Steel–concrete Composite Beams

Experimental studies on behavior of stud shear connectors subjected to cyclic loads

Experimental investigation of composite steel-concrete beams with corroded studs

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Experimental Study on the Shear Behavior of Friction Connections with Corrosion Damage

Behavior of Steel–Concrete Composite Beams with Corroded Shear Studs under Negative Bending Moment

Shear Capacity of Stud Shear Connectors with Initial Damage: Experiment, Fem Model and Theoretical Formulation

Monotonic and fatigue behavior of steel-concrete composite beams subjected to corrosion

Static Behavior and Theoretical Model of Stud Shear Connectors

Shear Performance of Reinforced Concrete Beams with Corroded Stirrups in Chloride Environment

Compressive Behaviour of Corroded Thin-Walled Circular Section Steel Stub Columns

Experimental study on mechanical behavior of stud shear connector with varions stud heights

Behavior of Corroded Thin-Walled Concrete-Filled Steel Tubular Stub Columns

Static Behavior of Multi-Stud Shear Connectors for Steel-Concrete Composite Bridge