Abstract:Simple and reliable mass production of platinum-based alloy catalysts with excellent activity and stability is an enormous challenge for the wide commercialization of proton-exchange membrane fuel cells (PEMFC), especially those with ultralow loading of Pt. Herein, an economical, highly durable, and efficient catalyst consisting of structurally ordered intermetallic Pt3Co alloy nanoparticles with ultralow Pt loading (1.4 wt %) supported on hierarchically porous carbon structure (three-dimensional, 3D Pt3Co/C) were synthesized with large-scale production by the NaCl-template-assisted approach. The obtained best sample, 3D Pt3Co/C#1, exhibited mass activities of 11.56 and 0.70 A mgPt–1 for oxygen reduction reactions (ORRs) in alkaline and acidic electrolytes, which are 60.8 and 6.4 times those of commercial Pt/C, respectively. Furthermore, the 3D Pt3Co/C#1 exhibited excellent stability both in acidic and alkaline electrolytes, with almost no decay of the half-wave potential after 5000 potential cycles. This work proposes a new high-yielding, simple, and environmentally friendly method to fabricate excellent Pt-based alloy electrocatalysts with ultralow loading of Pt, which opens up new hopes for the development of PEMFC.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c08839.SEM image of the sample 3D Pt3Co/C#1 after freeze-drying (Figure S1); XRD patterns of 3D Pt3Co/C#1 and 3D Pt/C (Figure S2); deconvoluted Pt 4f XPS spectra of 3D Pt3Co/C#2 and 3D Pt3Co/C#3 (Figure S3); deconvoluted Pt 4f XPS spectra of Pt3Co/C and 3D Pt/C (Figure S4); deconvolution of Pt 4f XPS spectra for all samples (Table S1); cyclic voltammograms in an N2-saturated 0.1 M HClO4 solution for 3D Pt3Co/C#1 and Pt/C (Figure S5); LSV curves of 3D Pt3Co/C#1 in O2-saturated 0.1 KOH and 0.1 M HClO4 electrolytes at room temperature under different rotating rates. The scan rate is 10 mV s–1 (Figure S6); Tafel plots of 3D Pt3Co/C#1 and 3D Pt/C (Figure S7); the number of transferred electrons of 3D Pt3Co/C#1 and Pt/C (Figure S8); the stability comparison of 3D Pt3Co/C#1 and the commercial Pt/C in O2-saturated 0.1 KOH and 0.1 M HClO4 electrolytes after 5000 cycles of ADT (Figure S9); SEM images of the sample 3D Pt3Co/C#1 after ADT (Figure S10); TEM image of the sample 3D Pt3Co/C#1 after ADT and the size distribution (Figure S11); XRD patterns of 3D Pt3Co/C#1 and after ADT (Figure S12); SEM images of the 3D Pt3Co/C-2 (Figure S13); LSV curves of 3D Pt3Co/C-2 recorded 0.1 M KOH and 0.1 M HClO4 electrolytes (Figure S14); the stability comparison of 3D Pt3Co/C#1 and the commercial Pt/C after 10 000 cycles of ADT (Figure S15); and comparison of ORR mass activities of the synthesized sample 3D Pt3Co/C#1 with reported precious catalysts (Table S2) (PDF)This article has not yet been cited by other publications.

A polyacrylonitrile copolymer-silica template for three-dimensional hierarchical porous carbon as a Pt catalyst support for the oxygen reduction reaction.

An elegant 3D-ordered hierarchically porous framework to anchor Pt nanocrystals for durable oxygen reduction reaction

A template approach to designing and synthesizing hierarchical porous carbon with tri-modal pore structure and its application for high performance oxygen reduction electrocatalyst support

General Synthesis of Three-Dimensionally Ordered Macro-/Mesoporous Materials and Their Electrocatalytic Applications

Synthesis of an improved hierarchical carbon-fiber composite as a catalyst support for platinum and its application in electrocatalysis

Hierarchical porous carbon materials prepared by direct carbonization of Al-PCP as a Pt-catalyst support for the oxygen reduction reaction

Templated-Assisted Synthesis of Structurally Ordered Intermetallic Pt 3 Co with Ultralow Loading Supported on 3D Porous Carbon for Oxygen Reduction Reaction

Three-Dimensional Ordered Honeycomb Nanostructure Anchored with Pt-N Active Sites via Self-Assembly of Block Copolymer: An Efficient Electrocatalyst towards Oxygen Reduction Reaction in Fuel Cells

Facile Synthesis of Hierarchically Ordered Porous Carbon Via in Situ Self-Assembly of Colloidal Polymer and Silica Spheres and Its Use As a Catalyst Support

Hollow Porous Carbon-Confined Atomically Ordered PtCo 3 Intermetallics for an Efficient Oxygen Reduction Reaction

Pyrolyzing soft template-containing poly(ionic liquid) into hierarchical N-doped porous carbon for electroreduction of carbon dioxide

Synthesis of Three-Dimensionally Ordered Macro-/Mesoporous Pt with High Electrocatalytic Activity by A Dual-Templating Approach

Cobalt-nitrogen-doped Ordered Macro-/Mesoporous Carbon for Highly Efficient Oxygen Reduction Reaction

A 3D Covalent Organic Framework with In-situ Formed Pd Nanoparticles for Efficient Electrochemical Oxygen Reduction

Self-Templating Synthesis of N/P/Fe Co-Doped 3D Porous Carbon for Oxygen Reduction Reaction Electrocatalysts in Alkaline Media

Engineering Three-Dimensional Interconnected Pores with Plentiful Edge Sites via a Confined Space for Enhanced Oxygen Reduction

Ordered Mesoporous Platinum@graphitic Carbon Embedded Nanophase As a Highly Active, Stable, and Methanol-Tolerant Oxygen Reduction Electrocatalyst.

Strongly Coupled 3D Hybrids of N‐doped Porous Carbon Nanosheet/CoNi Alloy‐Encapsulated Carbon Nanotubes for Enhanced Electrocatalysis

Hierarchically ordered macro‐mesoporous electrocatalyst with hydrophilic surface for efficient oxygen reduction reaction

Integrated Three-Dimensional Carbon Nanopolyhedron/Metal Sulfides: An Efficient Electrocatalyst Toward Oxygen Reduction Reaction

Multiheteroatom-Doped Porous Carbon Catalyst for Oxygen Reduction Reaction Prepared Using 3D Network of ZIF-8/Polymeric Nanofiber As a Facile-Doping Template.