Templated-Assisted Synthesis of Structurally Ordered Intermetallic Pt 3 Co with Ultralow Loading Supported on 3D Porous Carbon for Oxygen Reduction Reaction

Xiao-Feng Han,Nadia Batool,Wen-Tao Wang,Hao-Tian Teng,Li Zhang,Ruizhi Yang,Jing-Hua Tian

DOI: https://doi.org/10.1021/acsami.1c08839

2021-08-02

Abstract:Simple and reliable mass production of platinum-based alloy catalysts with excellent activity and stability is an enormous challenge for the wide commercialization of proton-exchange membrane fuel cells (PEMFC), especially those with ultralow loading of Pt. Herein, an economical, highly durable, and efficient catalyst consisting of structurally ordered intermetallic Pt3Co alloy nanoparticles with ultralow Pt loading (1.4 wt %) supported on hierarchically porous carbon structure (three-dimensional, 3D Pt3Co/C) were synthesized with large-scale production by the NaCl-template-assisted approach. The obtained best sample, 3D Pt3Co/C#1, exhibited mass activities of 11.56 and 0.70 A mgPt–1 for oxygen reduction reactions (ORRs) in alkaline and acidic electrolytes, which are 60.8 and 6.4 times those of commercial Pt/C, respectively. Furthermore, the 3D Pt3Co/C#1 exhibited excellent stability both in acidic and alkaline electrolytes, with almost no decay of the half-wave potential after 5000 potential cycles. This work proposes a new high-yielding, simple, and environmentally friendly method to fabricate excellent Pt-based alloy electrocatalysts with ultralow loading of Pt, which opens up new hopes for the development of PEMFC.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c08839.SEM image of the sample 3D Pt3Co/C#1 after freeze-drying (Figure S1); XRD patterns of 3D Pt3Co/C#1 and 3D Pt/C (Figure S2); deconvoluted Pt 4f XPS spectra of 3D Pt3Co/C#2 and 3D Pt3Co/C#3 (Figure S3); deconvoluted Pt 4f XPS spectra of Pt3Co/C and 3D Pt/C (Figure S4); deconvolution of Pt 4f XPS spectra for all samples (Table S1); cyclic voltammograms in an N2-saturated 0.1 M HClO4 solution for 3D Pt3Co/C#1 and Pt/C (Figure S5); LSV curves of 3D Pt3Co/C#1 in O2-saturated 0.1 KOH and 0.1 M HClO4 electrolytes at room temperature under different rotating rates. The scan rate is 10 mV s–1 (Figure S6); Tafel plots of 3D Pt3Co/C#1 and 3D Pt/C (Figure S7); the number of transferred electrons of 3D Pt3Co/C#1 and Pt/C (Figure S8); the stability comparison of 3D Pt3Co/C#1 and the commercial Pt/C in O2-saturated 0.1 KOH and 0.1 M HClO4 electrolytes after 5000 cycles of ADT (Figure S9); SEM images of the sample 3D Pt3Co/C#1 after ADT (Figure S10); TEM image of the sample 3D Pt3Co/C#1 after ADT and the size distribution (Figure S11); XRD patterns of 3D Pt3Co/C#1 and after ADT (Figure S12); SEM images of the 3D Pt3Co/C-2 (Figure S13); LSV curves of 3D Pt3Co/C-2 recorded 0.1 M KOH and 0.1 M HClO4 electrolytes (Figure S14); the stability comparison of 3D Pt3Co/C#1 and the commercial Pt/C after 10 000 cycles of ADT (Figure S15); and comparison of ORR mass activities of the synthesized sample 3D Pt3Co/C#1 with reported precious catalysts (Table S2) (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology