Influence of Filler and Fiber Properties and Their Ratio on the Dynamics and Strength of Reinforced Cylinders Under Internal Explosion

P. P. Lepikhin,V. A. Romashchenko,S. O. Tarasovska,O. S. Beiner,S. I. Trubachov

DOI: https://doi.org/10.1007/s11223-024-00703-y

IF: 0.667

2024-11-29

Strength of Materials

Abstract:Based on the known experimental data for two reinforcing fibers (transtropic carbon fiber T300 and isotropic glass fiber S2) and three isotropic matrices (fillers) (Epoxy, LY556, and 8511-7), the physical and mechanical elasticity and strength characteristics of six types of unidirectionally reinforced composites were determined by the Chamis analytical method in the range of change in the volume content V of reinforcing fibers from 0 to 0.65. Fibers, matrices, and composites made on their basis were considered elastic up to failure. It was determined by the numerical method that for composite cylinders with circular reinforcement under axisymmetric internal explosion, glass fibers S2 always provide greater strength at the same V compared to carbon fibers T300. In some cases, at the same V, the critical mass M of the explosive charge under reinforcement with S2 fibers increases by 30% compared to reinforcement with T300. The highest dynamic strength of the cylinders for both types of fibers is provided by the 8511-7 filler and the lowest by Epoxy. Of the six types of cylinders considered, the S2/8511-7 cylinder always has the highest dynamic strength at the same V, and the T300/Epoxy cylinder has the lowest. For all six types of the considered fiber/matrix combinations, the dynamic strength of the cylinders monotonically increases with an increase in the volume content of reinforcing fibers. The dependence M(V) is approximately linear for the T300/LY556 and T300/8511-7 cylinders and bilinear for the T300/Epoxy, S2/Epoxy, S2/LY556 and S2/8511-7 cylinders. The period of radial vibrations of shells decreases monotonically with an increase in V from 0 to 0.65: almost fivefold with reinforcement with T300 fibers, almost threefold with reinforcement with S2 fibers, and depends on the matrix type. The maximum deflection in these limiting states, even despite the increase in load proportional to M, also monotonically decreased with increase in V: 3- to 4-fold with reinforcement with T300 fibers and 2- to 2.5-fold with reinforcement with S2 fibers, depending on the type of the matrix. At constant V and load, the strength of the shells significantly depends on both the type of reinforcing fiber and the type of the matrix (filler), and the dynamics significantly depend on the type of fiber and insignificantly on the matrix type.

materials science, characterization & testing