Synthesis of carboxymethyl cellulose from coconut fibers and its application as solid polymer electrolyte membranes
Sun Theo Constan Lotebulo Ndruru,Aziz Daka Syamsaizar,Sandra Hermanto,Boy Chandra Sitanggang,Bibiana Dho Tawa,Aseel Ameer Kareem,Atika Nur Hayati,Benni Ramadhoni,Muhammad Ihsan Sofyan,Dicky Annas,Joni Prasetyo,Anita Marlina,Qolby Sabrina,Evi Yulianti,Sudaryanto,Deana Wahyuningrum,I Made Arcana
DOI: https://doi.org/10.1002/app.55629
IF: 3
2024-04-29
Journal of Applied Polymer Science
Abstract:Carboxymethyl cellulose (CMC) has been obtained by molecular structure modification of coconut fibers cellulose. CMC was blended with CMCh to find an outstanding matrix for solid polymer blend electrolyte membranes, where it was complexed with lithium acetate. The CMC/CMCh (80/20) + 20 wt% LiOAc exhibited the highest ionic conductivity (σ), ionic density (n), ion mobility (μ), and diffusion coefficient (D). These results fulfill the minimum standard for ionic conductivity lithium‐ion battery solid polymer electrolytes. Carboxymethyl cellulose (CMC) is one of the important cellulose derivatives, and it can be developed as a host polymer for solid polymer electrolyte (SPE) membrane. This study aimed to synthesis of CMC from coconut fiber cellulose and it was applied to prepare the SPE membranes. Cellulose isolation was conducted through the delignification and bleaching process, while the CMC synthesis was conducted through alkalization and carboxymethylation treatments. SPE membranes were prepared by blending CMC with carboxymethyl chitosan (CMCh) (80/20) and mixed with various weight percentages of LiOAc at room temperature. SPE membranes characterizations were conducted using FTIR, EIS, XRD, SEM, and tensile testing. Cellulose and CMC yields were 23.1% and 65.44%, respectively. Incorporating 20 wt% LiOAc into the CMC/CMCh (80/20) SPE membrane yielded the highest ionic conductivity of 1.37 × 10−3 S/cm.
polymer science