Multidimensional Dual-Carbon Skeleton Network Confined MnO x Anode Boosting High-Performance Lithium-Ion Hybrid Capacitors
Cheng Yue,Daping Qiu,Cuihua Kang,Min Li,Chuang Qiu,Liying Xian,Feng Wang,Ru Yang
DOI: https://doi.org/10.1021/acsaem.1c02116
IF: 6.4
2021-10-04
ACS Applied Energy Materials
Abstract:Manganese oxide with high theoretical specific capacity and intermediate reaction plateau is a promising anode candidate for lithium-ion hybrid capacitors (LIHCs). However, the sluggish kinetics and severe volume expansion have seriously hindered its practical progress. Herein, a mixed-valence manganese oxide confined by a dual-carbon skeleton network (MnOx@C-R) was successfully prepared. Owing to the synergistic effect of the introduction of the dual-carbon skeleton-network structure in a reducing atmosphere, the reasonable pore size distribution, crystallinity, and phase composition have been optimized. The material exhibits excellent lithium storage performance (778.2 mA h g–1 after 10 cycles at 0.1 A g–1), along with excellent rate performance (141.7 mA h g–1 at 5 A g–1) and stable cycling ability (402.4 m Ah g–1 for 1000 cycles at 1 A g–1). Moreover, further characterization displayed the change of the valence state of manganese during the charging/discharging, revealing the source of the excellent electrochemical performance of MnOx@C-R. Therefore, LIHCs were assembled using a MnOx@C-R anode and the activated carbon network with excellent energy density (151 Wh kg–1) and amazing power density (21.9 kW kg–1). This work supplies an alternative strategy for optimizing the lithium storage performance of manganese oxide.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c02116.Raman spectra of MnOx@C and MnOx@C-R; TG and DTG of MnOx@C-R; C 1s, O 1s, and N 1s XPS spectra of MnOx@C-R and MnOx@C; SEM images of MnOx; SEM images of MnOx@C; the DFT pore size distribution of MnOx@C-R and MnOx@C; microstructure analysis of MnOx@C; capacity contribution of different voltage ranges of MnOx@C-R; CV curves of MnOx and MnOx@C at 0.1 mV s–1; GCD curves of the first three cycles of MnOx and MnOx@C at 0.1 A g–1; cycling performance of MnOx-R; values of b plotted, and percentage of capacitance contribution at different scanning rates; electrochemical reaction mechanism at different voltage intervals; GITT test; EX-XPS spectra of powder samples and discharging/charging: full spectra and high-resolution O 1s; Nyquist plots of MnOx@C-R and MnOx@C; SEM images of GLC and AGLC; N2 adsorption–desorption isotherms of GLC and AGLC; electrochemical performance of AGLC cathode; GCD curves of LIHCs at different mass ratios of LIHCs; BET parameters of MnOx@C and MnOx@C-R; capacity and ratio of different voltage ranges of MnOx@C-R and MnOx@C; different voltage capacitive behavior at different scan rates; BET parameters of the AGLC and GLC (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels