Influence of MnCO 3 Additive on the Dielectric Properties of BaCuB 2 O 5 -Doped Ba 4.5 (nd 0.7 Sm 0.3 ) 9 Ti 18 O 54 Ceramics Sintered in a Reducing Atmosphere

Jun-Xiong Gao,Xiao-Hong Wang,Meng-Jie Wang,Xiao-Chuan Wang,Wen-Zhong Lu

DOI: https://doi.org/10.1007/s10854-016-4516-3

2016-01-01

Journal of Materials Science Materials in Electronics

Abstract:Sintered in a reducing atmosphere, the dielectric properties of Ba4.5(Nd0.7Sm0.3)9Ti18O54 (BNST) ceramics are deteriorated because of the ionized oxygen vacancies and conduction electrons. The feasibility of reduction resistance in BNST ceramics sintered in a reducing atmosphere was investigated in this work. Prompted by the example of BaTiO3 ceramics used in base-metal electrode multilayer ceramics capacitor, the effects of acceptor dopant MnCO3 on the microstructure, insulation resistivity (IR) and dielectric properties of BNST ceramics doped with 1 wt% BaCuB2O5 (BCB) sintered under a reducing atmosphere of moist N2-1%H2 were investigated. Results showed that MnCO3 effectively rendered BNST-BCB ceramics resistant to reduction. Mn ions completely substituted into the Ti4+ site of BNST at <1.5 wt% MnCO3 doping content, whereas secondary phases were formed with increased MnCO3 addition. Resistivity as high as 1012 Ω cm was effectively achieved in ceramics with the addition of >1.5 wt% MnCO3, and the dielectric constant (ε r ) of BNST-BCB was not obviously modified by the presence of additive. Moreover, 2 wt% MnCO3-doped BNST-1wt% BCB ceramics sintered in a reducing atmosphere exhibited attractive properties with ε r = 75.1, tanδ = 0.00115, TCC = −42.3 ppm/°C and IR = 4.56×1012 Ω cm.