High Energy Density, High Efficiency and Excellent Temperature Stability of Lead Free Mn–doped BaTiO3–Bi(Mg1/2Zr1/2)O3 Ceramics Sintered in a Reducing Atmosphere

Chaoqiong Zhu,Ziming Cai,Longtu Li,Xiaohui Wang

DOI: https://doi.org/10.1016/j.jallcom.2019.152498

IF: 6.2

2019-01-01

Journal of Alloys and Compounds

Abstract:Dielectric ceramics capacitors are of great interest duo to the improved energy-storage performance and temperature stability. However, to lower the cost and achieve mass production, the co-sintering of dielectric ceramics with base metals (such as Ni, Cu) is a huge challenge, since the co-sintering requires a reducing atmosphere to prevent the oxidization of base metals. Here in this work, the multivalence element Mn is doped into a relaxor ferroelectric ceramic system, i.e. 0.85BaTiO(3)-0.15Bi(Mg1/2Zr1/2)O-3 (BT-BMZ) ceramics through a conventional solid-state reaction method to realize the reducing atmosphere sintering. Effects of MnCO3 contents (0.05-0.25 wt%) on the energy-storage properties, temperature stabilities and electrical structures of the relaxor-ferroelectric BT-BMZ ceramics are investigated. The optimal energy-storage performance is found in 0.10 wt% MnCO3 doped BT-BMZ ceramics, with a high discharge energy density of 1.61 J/cm(3) and an ultrahigh energy efficiency of 94.3% under the applied electric field of 230 kV/cm. Further, the variation in energy density is less than 15% over the temperature range from 25 to 140 degrees C under 120 kV/cm. Additionally, the impedance spectroscopy is used to analyze the insulation mechanism of these reducing-atmosphere-sintered Mn-doped BT-BMZ ceramics. (C) 2019 Elsevier B.V. All rights reserved.