Hot Deformation Behavior and Dynamic Recrystallization Mechanism of Fe-18.2Mn-0.52C Twinning-Induced Plasticity Steel
Kairui Xue,Ke Qiao,Ting Zhang,Feng Gao,Jingchang Yao,Wen Wang,Kuaishe Wang
DOI: https://doi.org/10.1007/s11837-024-06678-0
2024-06-15
JOM
Abstract:The dynamic recrystallization behavior of twinning-induced plasticity (TWIP) steel during hot deformation is complex. In this work, hot compression experiments of TWIP steel were conducted on a Gleeble thermal-mechanical simulator under the temperature of 500–1000°C and the strain rate of 0.01–10 s −1 . The hot deformation behavior, microstructure evolution and dynamic recrystallization mechanism were investigated. Stress-strain curves showed a typical dynamic softening after peak stress at high temperatures and low strain rates. The developed Arrhenius constitutive equation considering the strain compensation could accurately predict the flow stress of TWIP steel. During hot deformation, the proportion and size of dynamic recrystallization grains increased with increasing temperature, while they first decreased and then increased with the increase of strain rate. At high temperature (1000°C) and high strain rate (10 s −1 ), the proportion of dynamic recrystallization grains was relatively high because of the high stored energy. In addition, annealing twin boundaries were generated during the nucleation and growth process of dynamic recrystallization grains. Discontinuous dynamic recrystallization was the main dynamic recrystallization mechanism of TWIP steel, and the continuous dynamic recrystallization and twin dynamic recrystallization were auxiliary nucleation mechanisms during hot deformation.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mineralogy,mining & mineral processing