Microstructural Evolution and Hot Deformation Behavior of Cu‐Containing Twinning‐Induced Plasticity Steel

Yang Feng,Xiaoyun Yuan,Yang Zhao,Liqing Chen
DOI: https://doi.org/10.1002/srin.202400335
IF: 2.1258
2024-08-21
steel research international
Abstract:It is of great research significance and application value to investigate the hot deformation behavior of Cu‐containing TWIP steels and to determine optimal hot working parameters. The constitutive equations and processing maps of Cu‐containing TWIP steels during hot deformation are established, focusing on the effects of deformation parameters and Cu elements on the hot deformation behavior and microstructural evolution. High manganese twinning‐induced plasticity (TWIP) steels with excellent strength and plasticity have promising applications in automotive manufacturing, but limited corrosion resistance affects their further development. Alloying with Cu is a viable solution to improve corrosion resistance. However, there remains a paucity of research concerning the effect of Cu on the hot deformation behavior of TWIP steels. So, the investigation of the recrystallization behavior and microstructural evolution in Fe‐23Mn‐6Cr‐3Al‐0.2C‐xCu (x = 0, 2.5) TWIP steels has been conducted using uniaxial hot compression test. The results reveal that Cu alloying exerts minimal influence on the high‐temperatur flow behavior, with dynamic recrystallization emerging as the predominant softening mechanism in Cu‐containing TWIP steels. However, owing to the drag effect of solute atoms, Cu alloying increases the activation energy for hot deformation and marginally reduces hot workability. Fine recrystallized grains in Cu‐containing TWIP steels can be achieved by hot deformation at lower temperatures and strain rate regions. The recrystallization behavior of Cu‐containing TWIP steels hot deformed at low temperatures and high strain rates is obviously inhibited by the increase of the activation energy and stacking fault energy, coupled with the hindering effect of Cu solute atoms clustered at grain boundaries on grain boundary migration.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?