Abstract:In this paper, we report a gallium‐based liquid metal patterning for paper‐based soft electronics. We propose a method which is rapid and straightforward liquid metal patterning on a printing paper using selective surface wetting properties obtained by waterproof agent coating and laser printed‐toner coating. A waterproof agent‐coated paper showed lyophilic properties, while a toner‐printed paper showed lyophobic properties against the liquid metal. On a printing paper, a waterproof agent was sprayed and a desired pattern was printed through a commercial laser printer where printing toner was coated. Then, a roller with a sponge soaked with liquid metal was rolled over on the paper to be printed with a desired pattern. Due to selective wetting property, the liquid metal was patterned on the paper. We believe that this is one of the most simple, straightforward yet quite versatile liquid metal patterning method. Various line patterns whose widths, spacing, and angles were varied to find out the minimum patterning size/shape of the liquid metal. The minimum line pattern width, spacing, and patternable angle were 50 μm, 200 μm, and 3 °, respectively. To demonstrate the versatility of shape patterning on the paper, a university symbol and a map shape were coated with the liquid metal. We demonstrated bending, folding, cutting and pasting, and burning of the light‐emitting diode (LED) circuit fabricated on paper. Deposition of 3 μm Parylene on top of the liquid metal patterned paper worked as a passivation layer, and no damage was noticed when the liquid metal pattern on paper was repeatedly folded and bent, and we finally demonstrated a pressure sensor using our proposed method by measuring resistance. This article is protected by copyright. All rights reserved.

Fabrication of User-Defined Copper Conductive Patterns Onto Paper Substrate for Flexible Electronics by Combining Wax Patterning with Electroless Plating

Preparation of Selective Conductive Copper Patterns by Pen-on-paper Writing Combined with Electroless Plating

Fabrication of dual-side metal patterns onto textile substrates for wearable electronics by combining wax-dot printing with electroless plating

High-Resolution Rapid Prototyping of Liquid Metal Electronics by Direct Writing on Highly Prestretched Substrates

Fabrication of paper-based conductive patterns for flexible electronics by direct-writing

Facial Fabrication of Paper-Based Flexible Electronics with Flash Foam Stamp Lithography

Fabrication of adhesion-enhanced and highly reliable copper circuits onto flexible substrates via a scribing–seeding–plating process

Fabrication of copper patterns on flexible substrate by patterning-adsorption-plating process.

Epoxy Resin-Assisted Cu Catalytic Printing for Flexible Cu Conductors on Smooth and Rough Substrates

Direct writing patterns for electroless plated copper thin film on plastic substrates

Synthesis of stable CucoreAgshell&Ag particles for direct writing flexible paper-based electronics

Patternable, High-Precision, Controllable Wettability Copper Layers for 3D Resin-Based Weather-Resistant Electronics and 3D Liquid Manipulation

Fabrication of Patterned Polymer Resists for Ion Etching by Using Dewetting

Fabrication of Conductive Copper Patterns Using Photocatalyst-activated Electroless Deposition

High-reproducibility, Flexible Conductive Patterns Fabricated with Silver Nanowire by Drop or Fit-to-flow Method

Preparation of Conductive Cu Patterns by Directly Writing Using Nano-Cu Ink

Directly Electroplated Metallization on Flexible Substrates Based on Silver Nanowire Conductive Composite for Wearable Electronics

A Rapid and Straightforward Liquid Metal Patterning Technique on Paper Using Laser Printer for Soft Electronics

Preparation of stable aqueous conductive ink with silver nanoflakes and its application on paper-based flexible electronics

3D Porous Polysiloxane Ion-Adsorption Films for Additive Fabrication of Conductive Patterns with High Adhesion

Towards Practical Application of Paper based Printed Circuits: Capillarity Effectively Enhances Conductivity of the Thermoplastic Electrically Conductive Adhesives