Transition of Blast Furnace Slag from Silicates-Based to Aluminates-Based: Viscosity

Dong Liang,Zhiming Yan,Xuewei Lv,Jie Zhang,Chenguang Bai

DOI: https://doi.org/10.1007/s11663-016-0676-z

2016-01-01

Metallurgical and Materials Transactions B

Abstract:The effect of Al 2 O 3 and the Al 2 O 3 /SiO 2 (A/S) ratio on the viscosity of the CaO-SiO 2 -Al 2 O 3 -MgO-TiO 2 slag system was studied in the present work. At a fixed CaO/SiO 2 (C/S) ratio of 1.20, 9 mass pct MgO, and 1 mass pct TiO 2 , the viscosity increases with an increase in Al 2 O 3 content at a range of 16 to 24 mass pct due to the polymerization of the aluminosilicate structures, while it decreases when the Al 2 O 3 is higher than 24 mass pct, which means that Al 2 O 3 acts as a network modifier at higher content. Increasing A/S from 0.47 to 0.92 causes a slight decrease in viscosity of the slags and has an opposite effect when A/S is more than 0.92. The free running temperature increases with the Al 2 O 3 content and appears to show a peak at an A/S ratio of 0.92. The change of the apparent activation energy is in accordance with the change of viscosity. When Al 2 O 3 content is more than 24 mass pct with low SiO 2 , CaO content ranges from 35 to 45 mass pct, and the slag transform from silicates-based to aluminates-based can still get a good operation region. Four different viscosity models were employed to predict the viscosity and RIBOUD’s model was found to be the best in predicting the viscosity by comparing the estimated viscosity with the measured viscosity.