Abstract:Al-doped spinel LiNi0.5Mn1.5O4 materials with different sites and contents were synthesized by rapid precipitation combined with hydrothermal treatment and calcination. The roles of Al on structural stability and electrochemical performance were studied by utilizing a series of techniques. XRD patterns indicated lower ion diffusion and no impure phased in doped samples. FT-IR and CV results reveal that Al-doped materials possess a Fd3̄m space group with increased disorder and increasing amounts of Mn3+. SEM and TEM equipped with EDS were used to characterize the regular morphology accompanied by a complete crystal structure and homogeneous distribution of elements. The Al content at the Ni, Mn, and Ni/Mn sites was optimized to be 5%, 3% and 5% (in total), respectively. The cycling stability was considerably enhanced at an ambient temperature (25 °C) and high temperature (55 °C). A typical Al dual-doped sample at Ni/Mn sites with 5% content delivered a reversible capacity of 113.5 mA h g-1 after 200 cycles at 0.5C. The discharge capacity at 5, 10 and 20C was 127.3, 125.5 and 123.1 mA h g-1, respectively. The discharge capacity remained at 126 mA h g-1 after 50 cycles (55 °C, 0.5C). Subsequent EIS and analytical results of the cycled electrode showed improved structural stability with a lower resistance, stable cathode/electrolyte interface, and reduced dissolution of Mn. These data further demonstrated the feasibility and reliability of preparing high-performance spinel LiNi0.5Mn1.5O4 cathode materials by doping with a suitable amount of Al.

Comparative Study of the Electrochemical Properties of Lini0.5mn1.5o4 Doped by Bivalent Ions (cu2+, Mg2+, and Zn2+)

Preparation and Electrochemical Properties of Li[Ni1/3Co1/3Mn1−x/3Zrx/3]O2 Cathode Materials for Li-ion Batteries

Electrochemical Performance Ni Doped Spinel LiMn2O4 Cathode for Lithium Ion Batteries

Effects of Doped Metal Ions of Different Oxidation States on Electrochemical Performance of LiMn_2O_4

Comparative Study of the Electrochemical Properties of P4332 and Fd3m Space Group of LiNi0.45Cu0.05Mn1.5O4 Cathode Materials

Electrochemical Investigations of the Lini0.45m0.10mn1.45o4 (M = Fe, Co, Cr) 5v Cathode Materials for Lithium Ion Batteries

Improving the Electrochemical Properties of High-Energy Cathode Material Lini0.5co0.2mn0.3o2 by Zr Doping and Sintering in Oxygen

Role of Al-doping with Different Sites Upon the Structure and Electrochemical Performance of Spherical LiNi0.5Mn1.5O4 Cathode Materials for Lithium-Ion Batteries

A comprehensive evaluation of Co, Ni, Cu and Zn doped manganese oxalate for lithium storage

Co-precipitation Synthesis and Characterization of Multiple Substituted Lithium Manganese Oxides in Lithium Ion Batteries

Synthesis and electrochemical performance of Mo-doped LiNi0.5Mn1.5O4 cathode material

Synthesis and electrochemical characterization of multi-cations doped spinel LiMn2O4 used for lithium ion batteries

Electrochemical Performance of LiMnPO4 by Fe and Zn Co-Doping for Lithium-Ion Batteries

Improvement of LiNi<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>O<sub>2</sub> Cathode Materials by Nano-MgO Doping

Sn-doped Li1.2Mn0.54Ni0.13Co0.13O2 cathode materials for lithium-ion batteries with enhanced electrochemical performance

Effect of Mn Doping on the Structure and Electrochemical Performance of LiNi0.7Co0.3O2

Effects of Al and Co doping on the structural stability and high temperature cycling performance of LiNi0.5Mn1.5O4 spinel cathode materials

LiNi_(0.5-x)Mg_xMn_(1.5)O_4(x=0,0.05) SYNTHESIZED BY LOW TEMPERATURE MOLTEN-SALT COMBUSTION METHOD AND ITS ELECTROCHEMICAL PERFORMANCE

Effect of Nb5+ doping on LiNi0.5Co0.25Mn0.25O2 cathode material

The effect on electrochemical properties of Ti4+ and V5+ doping in LiNi0.8Co0.1Mn0.1O2

Synthesis and Performance of Mn-doped Li3Fe2(PO4)3 Materials