Investigation on Hydrophobicity Transfer Property of Silicone Rubber under Heavy Contamination

Weian Ye,Zhidong Jia,Xilin Wang,Shitao Liu,Bo Wu

DOI: https://doi.org/10.1109/ceidp.2016.7785519

2016-01-01

Abstract:Silicone rubber (SIR) suffer from high contamination when insulators operate in heavy industrial area, thus further research about hydrophobicity transfer property under heavy contamination is needed. In this paper, NaCl was used as soluble salt and industrial kaolin was used as inert material to study hydrophobicity transfer property of room temperature vulcanized (RTV) SIR and high temperature vulcanized (HTV) SIR. Both RTV and HTV specimens were deposited with contaminant of different SDD, NSDD and different special contaminant composition. By continuously measuring static contact angle for 600h, the influence of SIR material, SDD, NSDD and contaminant composition to hydrophobicity transfer were compared and discussed. The measurement shows that RTV has much better hydrophobicity transfer behavior than the HTV. High SDD would result to crystalize of the salt on the surface, but it has no evident effect on the hydrophobicity transfer. High NSDD would slow down the hydrophobicity transfer speed, but its influence decrease over time. Different contaminant composition has significant influence to the hydrophobicity transfer process, reflected by different transfer speed and static contact angle at the steady state. ZnO, chemically pure kaolin and kieselguhr have much better hydrophobicity transfer behavior than industrial kaolin and Al2O3. Experiment with heavy contamination and 600h's hydrophobicity transfer shows that SIR and contaminant composition are the decisive factor to the hydrophobicity transfer. However, the relationship between contaminant com and hydrophobicity transfer needs further investigation.