Abstract:The SO2/NOX pollution in the flue gas of non-ferrous smelting is increasingly serious. At the same time, the accumulation of red mud (RM) in the aluminum industry and phosphorus sludge (PS) in the yellow phosphorus industry has caused serious harm to the environment. To remove SO2 and NOX from the non-ferrous smelting flue gas and realize the resource utilization of the above two solid wastes, an ultrasonic field was used in this study to strengthen the PS excited O3 process and RM wet desulfurization and denitrification process. In the process of O3 excitation, the response surface method (RSM) is used to obtain the optimal O3 excitation concentration, and the optimal reaction conditions are designed based on the response surface optimization model: T is 53.226 °C, power density is 0.4 W/cm2, PS concentration is 51.433 g/L, O3 formation concentration up to 250 ppm or more, which provides a theoretical basis for subsequent desulfurization and denitrification steps. It is proved that this study can replace the expensive traditional O3 generator and provide a basis for NOX removal in the following process. In addition, the optimum experimental conditions of ultrasonic enhanced RM desulfurization and denitrification process were also explored. Under ultrasonic frequency of 28 kHz, ultrasonic power density of 0.4 W/cm2, T of 50 °C, RM concentration of 15 g/L, and stirring intensity of 1000 rpm, the desulfurization efficiency of the reaction system can be maintained above 95 % within 250 min, and the denitrification efficiency can be maintained above 90 % within 250 min. The effect of desulfurization and denitrification in this study is much better than that of traditional methods. Finally, the reaction mechanism of ultrasonic enhanced O3 excitation and RM wet desulfurization and nitrogen removal was discussed by combining adsorption thermodynamics, isotherm, and kinetics. The results showed that the OH· free radicals generated by ultrasonic cavitation and the physical effects brought by emulsification had significant promoting effects.

The roles of red mud as desulfurization and denitrification in flue gas: A review

Advances in Technologies for in Situ Desulfurization of Biogas

Research on red mud-limestone modified desulfurization mechanism and engineering application

Applications of red mud as an environmental remediation material: A review

Red mud-based catalysts for the catalytic removal of typical air pollutants: A review

Novel Method for High-Performance Simultaneous Removal of NOx and SO2 by Coupling Yellow Phosphorus Emulsion with Red Mud

Enhanced NOx absorption in flue gas by wet oxidation of red mud and phosphorus sludge

Ultrasonic-enhanced Phosphorus Sludge Excited O3 Coupled Red Mud Simultaneous Desulfurization and Denitrification

A review of comprehensive utilization of red mud

Study on Desulfurization and Denitration of with Industry Solid Waste by Microwave

Manganese Ore-based Wet Flue-Gas Desulfurization: A Review

Toward sustainable green alumina production: A critical review on process discharge reduction from gibbsitic bauxite and large-scale applications of red mud

Application of red mud in carbon capture, utilization and storage (CCUS) technology

Research Progress on Comprehensive Utilization of Red Mud

Recent Advances in Elimination of SO2 and NOx from Flue Gas Employing Phosphorus Sludge and Phosphate Rock

The Large-Scale Sustainable Utilization Status of Bauxite Residue (red Mud): Challenges and Perspectives for China

Sodium ascorbate as additive in red mud slurry for simultaneous desulfurization and denitrification: Insights into the multiple influence factors and reaction mechanism

Characteristic, hazard and iron recovery technology of red mud - A critical review

Removal of SO2 and NOx from flue gas using mud-phosphorus slurry

Red mud with enhanced dealkalization performance by supercritical water technology for efficient SO 2 capture

Summary of Research Progress on Metallurgical Utilization Technology of Red Mud