Evidence for the transition from primary to peritectic phase growth during solidification of undercooled Ni-Zr alloy levitated by electromagnetic field

P. Lü,K. Zhou,H. P. Wang

DOI: https://doi.org/10.1038/srep39042

IF: 4.6

2016-01-01

Scientific Reports

Abstract:The Ni 83.25 Zr 16.75 peritectic alloy was undercooled by electromagnetic levitation method up to 198 K. The measured dendritic growth velocity shows a steep acceleration at a critical undercooling of Δ T crit = 124 K, which provides an evidence of the transition of the primary growth mode from Ni 7 Zr 2 phase to peritectic phase Ni 5 Zr. This is ascertained by combining the temperature-time profile and the evolution of the solidified microstructures. Below the critical undercooling, the solidified microstructure is composed of coarse Ni 7 Zr 2 dendrites, peritectic phase Ni 5 Zr and eutectic structure. However, beyond the critical undercooling, only a small amount of Ni 7 Zr 2 phase appears in the solidified microstructure. The dendritic growth mechanism of Ni 7 Zr 2 phase is mainly governed by solute diffusion. While, the dendritic growth mechanism of Ni 5 Zr phase is mainly controlled by thermal diffusion and liquid-solid interface atomic attachment kinetics.