Abstract:The metallurgical notch effect of weldment is critical for the structural integrity assessment and to avoid the premature failure especially at elevated temperature. The local nonhomogeneous microstructure located in heat affected zone (HAZ) and multi-pass weld metal area (WM) is one of the largest contributions for the material weakening of the entire weldment. Although the type IV failure related to the HAZ has been intensively discussed, few researchers focus on the creep damage on the weld metal. In fact, the limited long-term creep tests of welded joints conducted by Tabuchi et al. [4]. has emphasized the necessity of monitoring creep damage not only in the HAZ but also in the weld metal. In this article, the nonhomogeneous microstructure related creep damage of the CrMoV multi-pass weld metal is discussed in detail. Different fracture morphology subjected to different weld properties are compared with each other, including the distribution of creep cavities, the precipitates and the substructures of crept specimens sampled from weld pass metal in the welding direction (WP), the overlap of different weld passes (WPO) and multiple weld passes through the thickness direction (MWP). Further, the microscopic analysis on the heterogeneous creep damage behavior are conducted. It is found that the grain length difference perpendicular to the loading direction is the dominant reason for anisotropic creep damage of multi-pass weld metal. In addition, the mismatched creep properties of subzones in the multi-pass weld metal also affect the damage field distribution.

Effect of Notch Position on Creep Damage for Brazed Joint

Notch Effect on Creep Damage for Hastelloy C276-BNi2 Brazing Joint

A New Damage Evolution Model to Estimate the Creep Fracture Behavior of Brazed Joint under Multiaxial Stress

Creep Damage and Crack Initiation in P92–BNi2 Brazed Joint

Effects of Inner Defects on Creep Damage and Crack Initiation for a Brazed Joint

Creep Rupture Behavior of Hastelloy C276-BNi2 Brazed Joint

Effects of Creep Ductility and Notch Constraint on Creep Fracture Behavior in Notched Bar Specimens

Creep Damage and Interaction Behavior of Neighboring Notches in Components at Elevated Temperature

A More Appropriate FE Model to Predict the Creep Crack Initiation and Growth Behavior of Brazed Joint

Numerical simulation of creep notched bar of P91 steel

Creep Damage in 9-12% Cr Steel Notched Components: Microstructural Evolution and Stress State Dependence

Analysis of Creep Crack Growth Behavior of the Brazed Joint Using Continuum Damage Mechanics Approach

The Microstructure, Mechanical Properties and Fracture Behavior of Hastelloy C276-BNi2 Brazed Joint

The correlation between prior fatigue damage and remaining creep properties in a high chromium steel welded joint

Nonhomogeneous Microstructure Related Creep Damage of the CrMoV Multi-Pass Weld Metal

Effects of residual stress on creep damage and crack initiation in notched CT specimens of a Cr-Mo-V steel

Notch Effect on Structural Strength of Components at Elevated Temperature under Creep, Fatigue, and Creep-Fatigue Loading Conditions: Phenomenon and Mechanism

Remaining creep properties and fracture behaviour of P92 steel welded joint under prior low cycle fatigue loading

V-Notched Bar Creep Life Prediction: GH3536 Ni-Based Superalloy Under Multiaxial Stress State

Effects Of Notch Geometry On The Local Cleavage Fracture Stress Sigma(F)

Effects of HAZ widths on creep crack growth properties of welded joints