Abstract:Titania nanowire arrays have been deposited on Ti foils through direct oxidizing the Ti substrate with aqueous hydrogen peroxide solutions containing melamine and nitric acid, and the applicability of such nanowire arrays to back-illuminated dye-sensitized solar cells studied in parallel with titania nanotube arrays on Ti foils. The low-temperature nitrogen adsorption measurement reveals that the film with nanowires 25nm in diameter and 1μm in length possesses a BET specific surface area of 59.0m2g−1, a value much larger than 26m2g−1 calculated for the nanotube with an inner diameter of 80nm, an outer diameter of 120nm and a total length of 3μm. Assuming an indirect transition between band gaps, the nanowire film exhibits a bandgap of 3.1eV, slightly larger than that of 3.0eV for the nanotube one. A detailed electrochemical study suggests that, in comparison with the nanotube film, the nanowire one exhibits much lower saturated photocurrent and poorer conductivity under the Xe-lamp irradiation. However, when utilized to construct back-side illuminated dye-sensitized solar cells, the cell with the 2μm-thick nanowire photoanode possesses significantly higher efficiency than the one with the 3μm-thick nanotube photoanode. The relatively high energy conversion efficiency is contributed to the high specific surface area and the unique mesoporous structure of the titania nanowire arrays, which favors the adsorption of dye molecules.

Ultralong Rutile TiO2 Nanowire Arrays for Highly Efficient Dye-Sensitized Solar Cells.

Efficiency Improvement of TiO2 Nanowire Arrays Based Dye-Sensitized Solar Cells Through Further Enhancing the Specific Surface Area

Facile conversion of rutile titanium dioxide nanowires to nanotubes for enhancing the performance of dye-sensitized solar cells

Ultra-Long Anatase Tio2 Nanowire Arrays with Multi-Layered Configuration on Fto Glass for High-Efficiency Dye-Sensitized Solar Cells

Optimized Porous Rutile TiO2 Nanorod Arrays for Enhancing the Efficiency of Dye-Sensitized Solar Cells

Rutile TiO2 nano-branched arrays on FTO for dye-sensitized solar cells.

Densely Aligned Rutile Tio2 Nanorod Arrays with High Surface Area for Efficient Dye-Sensitized Solar Cells

Fabrication of Morphology Controllable Rutile TiO2 Nanowire Arrays by Solvothermal Route for Dye-Sensitized Solar Cells

Controllable Preparation of TiO2 Nanowire Arrays on Titanium Mesh for Flexible Dye-Sensitized Solar Cells

A novel approach to titania nanowire arrays as photoanodes of back-illuminated dye-sensitized solar cells

Oriented hierarchical single crystalline anatase TiO 2 nanowire arrays on Ti-foil substrate for efficient flexible dye-sensitized solar cells

A facile route to aligned TiO2 nanotube arrays on transparent conducting oxide substrates for dye-sensitized solar cells

Ultralong TiO2 (B) Nanowires/TiO2 Nanoparticles Composites for Rapid Electron Transport in Dye-Sensitized Solar Cells

Dye-Sensitized Solar Cells with Vertically Aligned Tio2 Nanowire Arrays Grown on Carbon Fibers

Realization of Ultra-Long Columnar Single Crystals in TiO2 Nanotube Arrays As Fast Electron Transport Channels for High Efficiency Dye-Sensitized Solar Cells

Solar Cells: Hierarchically Structured Nanotubes for Highly Efficient Dye‐Sensitized Solar Cells (adv. Mater. 22/2013)

ZnO/TiO 2 Core–shell Nanowire Arrays for Enhanced Dye-Sensitized Solar Cell Efficiency

Synthesis Of Long Tio2 Nanowire Arrays With High Surface Areas Via Synergistic Assembly Route For Highly Efficient Dye-Sensitized Solar Cells

Hydrothermal Fabrication of Hierarchically Anatase Tio2 Nanowire Arrays on Fto Glass for Dye-Sensitized Solar Cells

Ultralong Rutile TiO 2 Nanorod Arrays with Large Surface Area for CdS/CdSe Quantum Dot-sensitized Solar Cells

A General Method for Preparing Anatase TiO 2 Treelike-Nanoarrays on Various Metal Wires for Fiber Dye-Sensitized Solar Cells