Abstract:In this project, SBA-15 with a mesoporous pore channel structure was synthesized by a hydrothermal method and its characterization by XRD, SEM and TEM proved that the mesoporous channels had highly ordered. Ordered mesoporous supported composite metal oxide catalysts NiOx-CuOx/SBA-15 was prepared by Nanocasting using nickel nitrate and Copper nitrate as precursors. The influence of ratio of the mesoporous precursor Ni(NO3)2 and Cu(NO3)2 (1: 0, 3: 1, 2: 3, 2: 1, 1: 1, 2: 3, 0: 1), roasting temperature (300°C, 400°C, 500°C, 600°C, 700°C) and other influencing factors of mesoporous precursors for the selective oxidation of benzyl alcohol by supported composite metal oxides was investigated. The results represent that 88.85% could be achieved with the optimal calcination temperature of 500°C, nickel copper ratio of 2:1, Catalyst dosage of 1 g, reaction temperature of 90°C, reaction time of 5 h, 2.5 ml of Bnoh, 76.34% selectivity and 67.62% yield of Bzh. In the oxidation reaction with alcohol, reaction is difficult when there are electron withdrawing groups on aromatic rings; when there were no groups or electron groups on aromatic rings, active group containing alcohols had a higher conversion rate than that of Benzyl alcohol. In this composition, Ni-Cu composite oxides and their support catalysts with low raw material, simply preparation process and easy recovery were synthesized, furthermore under mild conditions, selective oxidation of benzyl alcohol in organic solvents has high catalytic activity and no environmental contamination. This manner is easy to operate, has high yield and high utilization rate of raw material that has certainly application value in chemical production of benzaldehyde.

Synthesis of Submicrometer-Sized Sn-Mcm-41 Particles and Their Catalytic Performance in Baeyer-Villiger Oxidation

In Situ Fabrication of Highly Active Γ-Mno2/smmno3 Catalyst for Deep Catalytic Oxidation of Gaseous Benzene, Ethylbenzene, Toluene, and O-Xylene.

Progress in Application of Tin-Containing Catalysts to Baeyer-Villiger Oxidation

Hydrothermal synthesis of tin containing mesoporous silicas and their catalytic performance over Baeyer–Villiger oxidation of cyclohexanone to ε-caprolactone: comparison of Sn/MCM-41 and Sn/SBA-15

Constructing Interconnected Hollow Mesopore Sn-Si Mixed Oxide Microspheres by Aerosol-Assisted Alkali Treatment with Enhanced Catalytic Performance in Baeyer-Villiger Oxidation

ZIF-8-derived Hollow Carbon Polyhedra with Highly Accessible Single Mn-N6 Sites As Peroxymonosulfate Activators for Efficient Sulfamethoxazole Degradation

Highly selective and clean synthesis of nopol over well-ordered mesoporous tin silicate catalysts

Characterization and Performance of SO42- / SnO2 / MCM-41 for α-pinene Isomerization

Synthesis of Bimetallic Modified Mesoporous Material and Its Application in Catalysis

Ag-modified SmMn2O5 Catalysts for CO and C3H8 Oxidation

The Synthesis of Sn-Containing Silicates Coated with Binaphthol and Their Specific Application for Catalytic Synthesis of 6-Hydroxyhexanoic Acid and Cyclohexylformate through Baeyer-Villiger Oxidation

Catalytic properties of mesoporous materials supported heteropoly acids for Baeyer-Villiger oxidation of cyclic ketones

Streamlined synthesis of iron and cobalt loaded MCM-48: High-performance heterogeneous catalysts for selective liquid-phase oxidation of toluene to benzaldehyde

Enhancing Methane Aromatization Performance by Reducing the Particle Size of Molybdenum Oxide

Preparation and Application of Metal Oxides/SBA-15 Mesoporous Composites as Catalysts for Selective Oxidation of benzyl alcohol

"Synthesis and characterization of mesoporous V-Mo-MCM-41 nanocatalysts: Enhancing efficiency in oxalic acid synthesis"

Tailoring the textural and component properties of Mo-Bi based catalysts for the selective oxidation of tert-butanol to methacrolein by the assistance of polymethymethacrylate

Morphology regulation of zero-valent iron nanosheets supported on microsilica for promoting peroxymonosulfate activation

Catalytic properties and nature of active centers of Cr/MCM-41 in catalytic abatement of sulfur-containing VOC of methanethiol

Construction of hierarchical Sn-ECNU-7 zeolite with MWW nanosheets for Baeyer-Villiger oxidation of bulky reactant

Synthesis, modification and application of layered double hydroxides as catalysts for Baeyer-Villiger oxidation